AKROMID®

A3 GF 35 3 black (1802)

PA66 GF35

AKROMID® A3 GF 35 3 black (1802) - 35% glass fiber reinforced PA 6.6, nucleated, technical parts in industrial engineering and automotive industry

Modulus

11.500MPa

Strength

180MPa

Impact

50kJ/m²

AKROMID® A3 GF 35 3 black (1802) - 35% glass fiber reinforced PA 6.6, nucleated, technical parts in industrial engineering and automotive industry

AKROMID®

A3 GM 20/10 S1 natural (1217)

PA66-I (GF20+GB10)

AKROMID® A3 GM 20/10 S1 natural (1217) - PA 6.6, impact modified, glass fiber and glass beads reinforced, good surface, adhesion modified, low warpage

Modulus

6.900MPa

Strength

130MPa

Impact

80kJ/m²

AKROMID® A3 GM 20/10 S1 natural (1217) - PA 6.6, impact modified, glass fiber and glass beads reinforced, good surface, adhesion modified, low warpage

AKROMID®

A3 GF 60 1 black (2395)

PA66 GF60

AKROMID® A3 GF 60 1 black (2395) - PA6.6, 60% glass fiber, highly reinforced, heat stabilised

Modulus

20.500MPa

Strength

260MPa

Impact

85kJ/m²

AKROMID® A3 GF 60 1 black (2395) - PA6.6, 60% glass fiber, highly reinforced, heat stabilised

AKROMID®

B3 GF 35 natural (2473)

PA6 GF35

AKROMID® B3 GF 35 natural (2473) - 35% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry

Modulus

11.500MPa

Strength

195MPa

Impact

100kJ/m²

AKROMID® B3 GF 35 natural (2473) - 35% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry

AKROMID®

A3 1 S3 black (2768)

PA66+PA6-I

AKROMID® A3 1 S3 black (2768) - PA66, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E

Modulus

2.600MPa

Strength

68MPa

Impact

180kJ/m²

AKROMID® A3 1 S3 black (2768) - PA66, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E

AKROMID®

A3 GM 20/10 4 WIT black (4529)

PA66 (GF20+GB10)

AKROMID® A3 GM 20/10 4 WIT black (4529) - 20% glass fibre, 10% glass bead, hydrolysis/chemical, polyamide 6.6, good surface, low warpage

Modulus

8.200MPa

Strength

175MPa

Impact

65kJ/m²

AKROMID® A3 GM 20/10 4 WIT black (4529) - 20% glass fibre, 10% glass bead, hydrolysis/chemical, polyamide 6.6, good surface, low warpage

AKROMID®

C3 GF 35 1 black (4668)

PA66+PA6 GF35

AKROMID® C3 GF 35 1 black (4668) - 35% glass fiber reinforced PA 6.6/6 blend, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

11.500MPa

Strength

200MPa

Impact

95kJ/m²

AKROMID® C3 GF 35 1 black (4668) - 35% glass fiber reinforced PA 6.6/6 blend, heat stabilised, technical parts in industrial engineering and automotive industry

178980

AKROMID®

UL

C3 GF 30 1 FR orange (7855)PA6+PA66 GF30 FR(40)

AKROMID® C3 GF 30 1 FR orange (7855) is a 30 % glass fiber reinforced, flame retardant and heat stabilised PA6/6.6 blend colored in orange similar to RAL 2003. Listed to UL 94 in all-colours, the material is based on a flame retardant system that is free of red phosphorus and halogens. Due to its good flowability, an improved surface quality is achieved. This grade is also suitable E&E applications (e.g. control cabinets), high voltage applications e-mobility as well as for railroad applications and meets the requirements for public transportation (EN 45545-2 R22/23/24 HL3).

Features

heat stabilised 130
electrically neutral
flame retardant
easy flow
E&E
public transportation

Regulatory

en45545-2ul

Properties

Modulus

10.600MPa

Strength

135MPa

Impact

65kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
10600 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
135 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
2,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
65 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
10 kJ/m²

Flammability

Burning rate

UL 94

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
V-0 Class
V-0 Class
V-0 Class
V-0 Class

GWFI

IEC 60695-2-12

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
960 °C
960 °C
960 °C
960 °C

GWIT

IEC 60695-2-13

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
725 °C
725 °C
725 °C
775 °C

HWI

UL 746A

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
0 PLC
0 PLC
0 PLC
0 PLC

HAI

UL 746A

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
0 PLC
0 PLC
0 PLC

Protection Train

EN 45545-2

R22/R23/R24 HL3

General properties

Density

ISO 1183

23°C
1,43 g/cm³

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
> 600 V

Dielectric strength

IEC 60243

3 mm
24 kV/mm

Inclined-Plane Tracking, IPT

ASTM D2303-13

1 kV

High voltage arc tracking rate (HVTR)

UL 746A

0 PLC

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.