AKROMIDĀ®

A3 GF 50 1 natural (1259)

PA66 GF50

AKROMIDĀ® A3 GF 50 1 natural (1259) - 50% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

16.700MPa

Strength

250MPa

Impact

105kJ/mĀ²

AKROMIDĀ® A3 GF 50 1 natural (1259) - 50% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMIDĀ®

A3 GF 35 3 black (1802)

PA66 GF35

AKROMIDĀ® A3 GF 35 3 black (1802) - 35% glass fiber reinforced PA 6.6, nucleated, technical parts in industrial engineering and automotive industry

Modulus

11.500MPa

Strength

180MPa

Impact

50kJ/mĀ²

AKROMIDĀ® A3 GF 35 3 black (1802) - 35% glass fiber reinforced PA 6.6, nucleated, technical parts in industrial engineering and automotive industry

AKROMIDĀ®

B3 GF 35 natural (2473)

PA6 GF35

AKROMIDĀ® B3 GF 35 natural (2473) - 35% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry

Modulus

11.500MPa

Strength

195MPa

Impact

100kJ/mĀ²

AKROMIDĀ® B3 GF 35 natural (2473) - 35% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry

AKROMIDĀ®

A3 GF 60 1 black (2395)

PA66 GF60

AKROMIDĀ® A3 GF 60 1 black (2395) - PA6.6, 60% glass fiber, highly reinforced, heat stabilised

Modulus

20.500MPa

Strength

260MPa

Impact

85kJ/mĀ²

AKROMIDĀ® A3 GF 60 1 black (2395) - PA6.6, 60% glass fiber, highly reinforced, heat stabilised

AKROMIDĀ®

B3 GF 30 1 L natural (4684)

PA6+PP GF30

AKROMIDĀ® B3 GF 30 1 L natural (4684) - PA6/PP-Blend 30% glass fibre reinforced, lower density, cost reduced, calcium chloride

Modulus

8.500MPa

Strength

150MPa

Impact

70kJ/mĀ²

AKROMIDĀ® B3 GF 30 1 L natural (4684) - PA6/PP-Blend 30% glass fibre reinforced, lower density, cost reduced, calcium chloride

AKROMIDĀ®

C3 GF 35 1 black (4668)

PA66+PA6 GF35

AKROMIDĀ® C3 GF 35 1 black (4668) - 35% glass fiber reinforced PA 6.6/6 blend, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

11.500MPa

Strength

200MPa

Impact

95kJ/mĀ²

AKROMIDĀ® C3 GF 35 1 black (4668) - 35% glass fiber reinforced PA 6.6/6 blend, heat stabilised, technical parts in industrial engineering and automotive industry

AKROLOYĀ®

PA GF 50 natural (6414)

PA66+PA6I/6T GF50

AKROLOYĀ® PA GF 50 natural (6414) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

Modulus

17.000MPa

Strength

275MPa

Impact

110kJ/mĀ²

AKROLOYĀ® PA GF 50 natural (6414) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

178980

AKROMIDĀ®

A3 GF 35 2 black (7226)PA66 GF35

AKROMIDĀ® A3 GF 35 2 black (7226) is a 35% glass fiber reinforced polyamide 6.6. It is characterised by high stiffness and strength. Furthermore, the material is heat and UV-stabilised and therefore perfectly suitable for technical parts in industrial engineering and in the automotive industry.

Features

UV-stabilised

Properties

Modulus

11.500MPa

Strength

215MPa

Impact

90kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
11500 MPa
8400 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
215 MPa
145 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3 %
5 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
90 kJ/mĀ²
100 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
15 kJ/mĀ²
19 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
255 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
260 Ā°C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
220 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 Ā°C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,4 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,8 - 2,0 %

Water absorption

ISO 62

23Ā°C, saturated
4,7 - 5,3 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,6 - 0,8 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
conditioned
1013 ā„¦ x cm
1010 ā„¦ x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
1012 ā„¦
1010 ā„¦

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.