AKROMID®

B3 GF 30 9 black (8643)

PA6 GF30

AKROMID® B3 GF 30 9 black (8643) - 30% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

10.000MPa

Strength

150MPa

Impact

55kJ/m²

AKROMID® B3 GF 30 9 black (8643) - 30% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

B25 GF 60 1 LA black (8281)

PA6 GF60

AKROMID® B25 GF 60 1 LA black (8281) is a 60% glass fibre reinforced, heat slightly stabilised, easy flowing polyamide 6 with very high stiffness and strength, lasermarkable.

Modulus

21.000MPa

Strength

255MPa

Impact

95kJ/m²

AKROMID® B25 GF 60 1 LA black (8281) is a 60% glass fibre reinforced, heat slightly stabilised, easy flowing polyamide 6 with very high stiffness and strength, lasermarkable.

AKROLOY®

UL

PARA GF 50 HU black (8596)

PARA GF50

AKROLOY® PARA GF 50 HU black (8596) - PARA, 50% GF, highed modulus and strength, easy flowing, listed at UL in all colors, metal substitute

Modulus

19.700MPa

Strength

295MPa

Impact

78kJ/m²

AKROLOY® PARA GF 50 HU black (8596) - PARA, 50% GF, highed modulus and strength, easy flowing, listed at UL in all colors, metal substitute

AKROMID®

B28 GM 10/20 1 LA black (4790)

PA6 (GF10+GB20)

AKROMID® B28 GM 10/20 1 LA black (4790) - PA6, 10% glass fibre, 20% glass bead, heat stabilised, laser markable, easy flowing, good surface, reduced warpage.

Modulus

5.700MPa

Strength

110MPa

Impact

30kJ/m²

AKROMID® B28 GM 10/20 1 LA black (4790) - PA6, 10% glass fibre, 20% glass bead, heat stabilised, laser markable, easy flowing, good surface, reduced warpage.

AKROLOY®

UL

PARA GF 60 HU natural (8516)

PARA GF60

AKROLOY® PARA GF 60 HU natural (8516) - PARA, 60% GF, high modulus and strength, easy flowing, listed at UL in all colors, metal substitute

Modulus

24.000MPa

Strength

300MPa

Impact

80kJ/m²

AKROLOY® PARA GF 60 HU natural (8516) - PARA, 60% GF, high modulus and strength, easy flowing, listed at UL in all colors, metal substitute

AKROMID®

UL
Preliminary

B28 GF 25 9 FR orange (8644)

PA6 GF25 FR(40)

AKROMID® B28 GF 25 9 FR orange (8644) - PA6, 25% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, RAL 2003, e-mobility.

Modulus

9.000MPa

Strength

135MPa

Impact

81kJ/m²

AKROMID® B28 GF 25 9 FR orange (8644) - PA6, 25% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, RAL 2003, e-mobility.

AKROMID®

A3 GF 35 3 black (1802)

PA66 GF35

AKROMID® A3 GF 35 3 black (1802) - 35% glass fiber reinforced PA 6.6, nucleated, technical parts in industrial engineering and automotive industry

Modulus

11.500MPa

Strength

180MPa

Impact

50kJ/m²

AKROMID® A3 GF 35 3 black (1802) - 35% glass fiber reinforced PA 6.6, nucleated, technical parts in industrial engineering and automotive industry

167880

AKROMID®

Preliminary
Internal

T9 GF 15 FR LA black (8197)PPA GF15 FR(40)

AKROMID® T9 GF 15 FR LA black (8197) is a flame retardant, 15% glass fibre reinforced polyphthalamide. The product is based on PA9T and has a significantly lower moisture absorption compared to conventional PA6T grades. As a result, the glass transition area is much more constant and even in the conditioned state, the product impresses with its medium strength and stiffness. Due to its high temperature and media resistance, this material is suitable for technical components that come into contact with chemicals. The flame retardant system is free of red phosphorus and halogens. This type is laser-markable.

Features

flame retardant
laser markable

Properties

Modulus

6.000MPa

Strength

107MPa

Impact

48kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
6000 MPa
6000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
107 MPa
101 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,2 %
2,8 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
48 kJ/m²
40 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
6 kJ/m²
6 kJ/m²

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
305 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
V-0 Class
V-0 Class
V-0 Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
960 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,26 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0.2 - 0.4 %
0.6 - 0.8 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
conditioned
1014 Ω x cm
1014 Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
1013 Ω
1012 Ω

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more