AKROMID®
B3 GF 30 9 black (8643)
PA6 GF30
AKROMID® B3 GF 30 9 black (8643) - 30% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry
10.000MPa
150MPa
55kJ/m²
AKROMID® B3 GF 30 9 black (8643) - 30% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry
AKROMID®
B25 GF 60 1 LA black (8281)
PA6 GF60
AKROMID® B25 GF 60 1 LA black (8281) is a 60% glass fibre reinforced, heat slightly stabilised, easy flowing polyamide 6 with very high stiffness and strength, lasermarkable.
21.000MPa
255MPa
95kJ/m²
AKROMID® B25 GF 60 1 LA black (8281) is a 60% glass fibre reinforced, heat slightly stabilised, easy flowing polyamide 6 with very high stiffness and strength, lasermarkable.
AKROLOY®
PARA GF 50 HU black (8596)
PARA GF50
AKROLOY® PARA GF 50 HU black (8596) - PARA, 50% GF, highed modulus and strength, easy flowing, listed at UL in all colors, metal substitute
19.700MPa
295MPa
78kJ/m²
AKROLOY® PARA GF 50 HU black (8596) - PARA, 50% GF, highed modulus and strength, easy flowing, listed at UL in all colors, metal substitute
AKROMID®
B28 GM 10/20 1 LA black (4790)
PA6 (GF10+GB20)
AKROMID® B28 GM 10/20 1 LA black (4790) - PA6, 10% glass fibre, 20% glass bead, heat stabilised, laser markable, easy flowing, good surface, reduced warpage.
5.700MPa
110MPa
30kJ/m²
AKROMID® B28 GM 10/20 1 LA black (4790) - PA6, 10% glass fibre, 20% glass bead, heat stabilised, laser markable, easy flowing, good surface, reduced warpage.
AKROLOY®
PARA GF 60 HU natural (8516)
PARA GF60
AKROLOY® PARA GF 60 HU natural (8516) - PARA, 60% GF, high modulus and strength, easy flowing, listed at UL in all colors, metal substitute
24.000MPa
300MPa
80kJ/m²
AKROLOY® PARA GF 60 HU natural (8516) - PARA, 60% GF, high modulus and strength, easy flowing, listed at UL in all colors, metal substitute
AKROMID®
B28 GF 25 9 FR orange (8644)
PA6 GF25 FR(40)
AKROMID® B28 GF 25 9 FR orange (8644) - PA6, 25% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, RAL 2003, e-mobility.
9.000MPa
135MPa
81kJ/m²
AKROMID® B28 GF 25 9 FR orange (8644) - PA6, 25% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, RAL 2003, e-mobility.
AKROMID®
A3 GF 35 3 black (1802)
PA66 GF35
AKROMID® A3 GF 35 3 black (1802) - 35% glass fiber reinforced PA 6.6, nucleated, technical parts in industrial engineering and automotive industry
11.500MPa
180MPa
50kJ/m²
AKROMID® A3 GF 35 3 black (1802) - 35% glass fiber reinforced PA 6.6, nucleated, technical parts in industrial engineering and automotive industry
AKROMID®
A3 GF 30 6 ECO black (8160)PA6.6 GF30
AKROMID® A3 GF 30 6 ECO black (8160) is a 30% glass fibre-reinforced, inorganically heat-stabilised polyamide 6.6. The material is suitable for technical components in mechanical engineering and the automotive industry with demands for high stiffness and strength. The formulations of the sustainable ECO products are partly based on regenerated post-industrial feedstock (at least 30 weight-% by recipe) and thus contribute to reducing the consumption of valuable raw materials. This type is laser-markable.
Features
Properties
9.000MPa
150MPa
50kJ/m²
Sustainability
Recycled content
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Temperature of deflection under load HDT/B
ISO 75
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Molding shrinkage
ISO 294-4
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.