P3 GF 30 LA black (6969)PBT GF 30

PRECITE® P3 GF 30 LA black (6969) is a 30% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with high stiffness and toughness as well as high dimensional and chemical resistance, laser markable.

Features

laser markable

Properties

Modulus

10.000MPa

Strength

145MPa

Impact

68kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
10000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
145 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
3 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
10500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
230 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
68 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
11 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
205 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
225 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

General properties

Density

ISO 1183

23°C
1,53 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,2 %

Water absorption

ISO 62

23°C, saturated
0,4 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 %
0,9 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
400 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.