AKROMIDĀ®

B3 GF 30 9 black (8643)

PA6 GF30

AKROMIDĀ® B3 GF 30 9 black (8643) - 30% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

10.000MPa

Strength

150MPa

Impact

55kJ/mĀ²

AKROMIDĀ® B3 GF 30 9 black (8643) - 30% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMIDĀ®

B28 GM 10/20 1 LA black (4790)

PA6 (GF10+GB20)

AKROMIDĀ® B28 GM 10/20 1 LA black (4790) - PA6, 10% glass fibre, 20% glass bead, heat stabilised, laser markable, easy flowing, good surface, reduced warpage.

Modulus

5.700MPa

Strength

110MPa

Impact

30kJ/mĀ²

AKROMIDĀ® B28 GM 10/20 1 LA black (4790) - PA6, 10% glass fibre, 20% glass bead, heat stabilised, laser markable, easy flowing, good surface, reduced warpage.

AKROMIDĀ®

B3 GF 35 1 natural (2465)

PA6 GF35

AKROMIDĀ® B3 GF 35 1 natural (2465) - 35% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

11.500MPa

Strength

195MPa

Impact

100kJ/mĀ²

AKROMIDĀ® B3 GF 35 1 natural (2465) - 35% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMIDĀ®

A3 GF 50 1 black (2387)

PA66 GF50

AKROMIDĀ® A3 GF 50 1 black (2387) - 50% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

16.700MPa

Strength

250MPa

Impact

105kJ/mĀ²

AKROMIDĀ® A3 GF 50 1 black (2387) - 50% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMIDĀ®

Preliminary

B28 GF 30 natural (4826)

PA6 GF30

AKROMIDĀ® B28 GF 30 natural (4826) - 30% glass fiber reinforced PA 6, easy flowing, technical parts in industrial engineering and automotive industry

Modulus

9.500MPa

Strength

180MPa

Impact

90kJ/mĀ²

AKROMIDĀ® B28 GF 30 natural (4826) - 30% glass fiber reinforced PA 6, easy flowing, technical parts in industrial engineering and automotive industry

AKROTEKĀ®

RA GFM 15/25 black (8216)

PA6 (GF15+MD25)

AKROTEKĀ® RA GFM 15/25 black (8216) - PA 6, 15% glass fiber reinforced, 25% mineral filled, radar absorption, 76-81 GHz

Modulus

8.500MPa

Strength

120MPa

Impact

50kJ/mĀ²

AKROTEKĀ® RA GFM 15/25 black (8216) - PA 6, 15% glass fiber reinforced, 25% mineral filled, radar absorption, 76-81 GHz

AKROMIDĀ®

A3 GM 20/10 4 WIT black (4529)

PA66 (GF20+GB10)

AKROMIDĀ® A3 GM 20/10 4 WIT black (4529) - 20% glass fibre, 10% glass bead, hydrolysis/chemical, polyamide 6.6, good surface, low warpage

Modulus

8.200MPa

Strength

175MPa

Impact

65kJ/mĀ²

AKROMIDĀ® A3 GM 20/10 4 WIT black (4529) - 20% glass fibre, 10% glass bead, hydrolysis/chemical, polyamide 6.6, good surface, low warpage

167877

AKROTEKĀ®

PK-VM 8 black (6466)PK

AKROTEKĀ® PK-VM 8 black (6466) is an unreinforced, low viscous polyketone. The material is suitable for drinking water contact and meets the requirements according to ACS, WRAS as well as NSF61. Moreover the material corresponds to the European food guideline EU 10/2011. Conformity to the American FDA 21 CFR guideline does NOT exist.

Features

hydrolysis / chemically stabilised

Regulatory

acseu102011nsf-coldnsf-hotwras

Properties

Modulus

1.600MPa

Strength

60MPa

Impact

180kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
1600 MPa
1600 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
60 MPa
60 MPa

Tensile strain at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
> 15 %
> 15 %

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
> 100 %
> 100 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
no break
no break

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
12 kJ/mĀ²
12 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
100 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,24 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
0,8 - 0,9 %

Molding shrinkage

ISO 294-4

flow
transverse
1,7 - 1,9 %
1,9 - 2,1 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
1013 ā„¦ x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1013 ā„¦

Rheological Properties

MVR

ISO 1133

240Ā°C/2,16kg
50 cmĀ³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.