AKROMID®

B3 GF 30 1 natural (2464)

PA6 GF30

AKROMID® B3 GF 30 1 natural (2464) - 30% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

10.300MPa

Strength

185MPa

Impact

95kJ/m²

AKROMID® B3 GF 30 1 natural (2464) - 30% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

UL
Preliminary

B28 GF 35 9 FR black (8189)

PA6 GF35 FR(40)

AKROMID® B28 GF 35 9 FR black (8189) - PA6, 35% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.

Modulus

12.600MPa

Strength

152MPa

Impact

70kJ/m²

AKROMID® B28 GF 35 9 FR black (8189) - PA6, 35% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.

AKROMID®

Preliminary

NEXT 5.10 3 GF 30 natural (8406)

PA5.10 GF30

AKROMID® NEXT 5.10 3 GF 30 natural (8406) - 100% biobased and HMD-free PA 5.10 with high strength.

Modulus

8.300MPa

Strength

160MPa

Impact

72kJ/m²

AKROMID® NEXT 5.10 3 GF 30 natural (8406) - 100% biobased and HMD-free PA 5.10 with high strength.

AKROMID®

B3 GF 40 S1 LA black (7614)

PA6-I GF40

AKROMID® B3 GF 40 S1 LA black (7614) - PA 6, 40% glass fiber reinforced, impact modified, laser markable, good surface, housings, covers, automotive

Modulus

12.000MPa

Strength

185MPa

Impact

100kJ/m²

AKROMID® B3 GF 40 S1 LA black (7614) - PA 6, 40% glass fiber reinforced, impact modified, laser markable, good surface, housings, covers, automotive

AKROMID®

Preliminary

NEXT G3 GF 30 1 natural (8085)

PA6.9 GF30

AKROMID® NEXT G3 GF 30 1 natural (8085) - partly bio-based PA 6.9, low moisture absorption, increased chemical resistance.

Modulus

8.600MPa

Strength

160MPa

Impact

80kJ/m²

AKROMID® NEXT G3 GF 30 1 natural (8085) - partly bio-based PA 6.9, low moisture absorption, increased chemical resistance.

AKROMID®

B25 GF 60 1 LA black (8281)

PA6 GF60

AKROMID® B25 GF 60 1 LA black (8281) is a 60% glass fibre reinforced, heat slightly stabilised, easy flowing polyamide 6 with very high stiffness and strength, lasermarkable.

Modulus

21.000MPa

Strength

255MPa

Impact

95kJ/m²

AKROMID® B25 GF 60 1 LA black (8281) is a 60% glass fibre reinforced, heat slightly stabilised, easy flowing polyamide 6 with very high stiffness and strength, lasermarkable.

AKROMID®

B28 GM 10/20 1 LA black (4790)

PA6 (GF10+GB20)

AKROMID® B28 GM 10/20 1 LA black (4790) - PA6, 10% glass fibre, 20% glass bead, heat stabilised, laser markable, easy flowing, good surface, reduced warpage.

Modulus

5.700MPa

Strength

110MPa

Impact

30kJ/m²

AKROMID® B28 GM 10/20 1 LA black (4790) - PA6, 10% glass fibre, 20% glass bead, heat stabilised, laser markable, easy flowing, good surface, reduced warpage.

156780

AKROTEK®

PK-HM 8 black (6246)PK

AKROTEK® PK-HM 8 black (6246) is an unreinforced, high viscosity polyketone. The material is suitable for drinking water contact and meets the requirements according to ACS and WRAS. Moreover the material corresponds to the European food guideline EU 10/2011, but not to the American FDA 21 CFR.

Features

hydrolysis / chemically stabilised

Regulatory

acseu102011wras

Properties

Modulus

1.600MPa

Strength

60MPa

Impact

180kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
1600 MPa
1600 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
60 MPa
60 MPa

Tensile strain at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
21 %
21 %

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
> 300 %
> 300 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
1700 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
62 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
no break
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
21 kJ/m²
21 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
100 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,24 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,8 - 0,9 %

Water absorption

ISO 62

23°C, saturated
2,0 - 2,4 %

Molding shrinkage

ISO 294-4

flow
transverse
1,7 - 1,9 %
1,9 - 2,1 %

Rheological Properties

MVR

ISO 1133

240°C/2,16kg
6 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.