AKROMID®

B3 CGM 15/20 1 LA black (8058)

PA6 (CF15+GF20)

AKROMID® B3 CGM 15/20 1 LA black (8058) - PA 6, 20% glass fiber reinforced, 15% carbon fiber reinforced, heat stabilized, electrical conductivity, laser marking, fuel filter housing, fulfills GMW 17683

Modulus

17.000MPa

Strength

195MPa

Impact

70kJ/m²

AKROMID® B3 CGM 15/20 1 LA black (8058) - PA 6, 20% glass fiber reinforced, 15% carbon fiber reinforced, heat stabilized, electrical conductivity, laser marking, fuel filter housing, fulfills GMW 17683

AKROMID®

B3 GF 30 1 black (2485)

PA6 GF30

AKROMID® B3 GF 30 1 black (2485) - 30% glass fiber reinforced PA 6, heat stabilised, industrial engineering, automotive, also as biomass-balanced and chemical recycled PA6.

Modulus

10.300MPa

Strength

185MPa

Impact

75kJ/m²

AKROMID® B3 GF 30 1 black (2485) - 30% glass fiber reinforced PA 6, heat stabilised, industrial engineering, automotive, also as biomass-balanced and chemical recycled PA6.

AKROMID®

UL
Preliminary

B28 GF 25 9 FR natural (8066)

PA6 GF25 FR(40)

AKROMID® B28 GF 25 9 FR natural (8066) - PA6, 25% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.

Modulus

8.900MPa

Strength

138MPa

Impact

83kJ/m²

AKROMID® B28 GF 25 9 FR natural (8066) - PA6, 25% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.

AKROMID®

UL
Preliminary

B28 GF 30 9 FR black (8342)

PA6 GF30 FR(40)

AKROMID® B28 GF 30 9 FR black (8342) - PA6, 30% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.

Modulus

10.200MPa

Strength

148MPa

Impact

75kJ/m²

AKROMID® B28 GF 30 9 FR black (8342) - PA6, 30% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.

AKROMID®

B3 GF 40 S1 LA black (7614)

PA6-I GF40

AKROMID® B3 GF 40 S1 LA black (7614) - PA 6, 40% glass fiber reinforced, impact modified, laser markable, good surface, housings, covers, automotive

Modulus

12.000MPa

Strength

185MPa

Impact

100kJ/m²

AKROMID® B3 GF 40 S1 LA black (7614) - PA 6, 40% glass fiber reinforced, impact modified, laser markable, good surface, housings, covers, automotive

AKROMID®

Preliminary

NEXT 5.10 3 GF 30 natural (8406)

PA5.10 GF30

AKROMID® NEXT 5.10 3 GF 30 natural (8406) - 100% biobased and HMD-free PA 5.10 with high strength.

Modulus

8.300MPa

Strength

160MPa

Impact

72kJ/m²

AKROMID® NEXT 5.10 3 GF 30 natural (8406) - 100% biobased and HMD-free PA 5.10 with high strength.

AKROMID®

B25 GF 60 1 LA black (8281)

PA6 GF60

AKROMID® B25 GF 60 1 LA black (8281) is a 60% glass fibre reinforced, heat slightly stabilised, easy flowing polyamide 6 with very high stiffness and strength, lasermarkable.

Modulus

21.000MPa

Strength

255MPa

Impact

95kJ/m²

AKROMID® B25 GF 60 1 LA black (8281) is a 60% glass fibre reinforced, heat slightly stabilised, easy flowing polyamide 6 with very high stiffness and strength, lasermarkable.

156780

AKROMID®

A3 GK 30 natural (3689)PA66 GB30

AKROMID® A3 GK 30 natural (3689) is a PA 6.6 filled with 30% glass beads. It is characterized by a high surface quality and low tendency to warp, which makes it suitable for use in technically demanding components in mechanical engineering and in the automotive industry.

Features

recycled content
low warpage

Properties

Modulus

5.000MPa

Strength

90MPa

Impact

28kJ/m²

Sustainability

Recycled content

30 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
5000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
90 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
4 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
4300 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
140 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
6,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
30°C | d.a.m.
-
28 kJ/m²
22 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
30°C | d.a.m.
-
4 kJ/m²
3 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
100 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
225 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
650 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,35 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,0 %

Molding shrinkage

ISO 294-4

flow
transverse
1,1 %
1,3 %

Electrical Properties

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1013 Ω

Comparative tracking index

IEC 60112

Test liquid A
500 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more