HEADER Granulat 1920x700

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/mĀ²
558 Compounds found
Recommended Ā 
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

PRECITEĀ®

P3 S1 black (7522)

PBT I

PRECITEĀ® P3 S1 black (7522) - PBT unreinforced, impact modified, good dimensional stability.

Modulus

1.750MPa

Strength

40MPa

Impact

180kJ/mĀ²

PRECITEĀ® P3 S1 black (7522) - PBT unreinforced, impact modified, good dimensional stability.

AKROMIDĀ®

B28 GF 30 2 black (7059)

PA6 GF30

AKROMIDĀ® B28 GF 30 2 black (7059) - PA 6, 30% glass fiber reinforced, easy flowing, UV and heat stabilised, outdoor applications

Modulus

10.000MPa

Strength

180MPa

Impact

70kJ/mĀ²

AKROMIDĀ® B28 GF 30 2 black (7059) - PA 6, 30% glass fiber reinforced, easy flowing, UV and heat stabilised, outdoor applications

AKROMIDĀ®

UL
Preliminary

B28 GF 25 9 FR natural (8066)

PA6 GF25 FR(40)

AKROMIDĀ® B28 GF 25 9 FR natural (8066) - PA6, 25% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.

Modulus

8.900MPa

Strength

138MPa

Impact

83kJ/mĀ²

AKROMIDĀ® B28 GF 25 9 FR natural (8066) - PA6, 25% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.

AKROMIDĀ®

UL
Preliminary

B28 GF 25 9 FR black (8250)

PA6 GF25 FR(40)

AKROMIDĀ® B28 GF 25 9 FR black (8250) - PA6, 25% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, UV stabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.

Modulus

9.000MPa

Strength

135MPa

Impact

81kJ/mĀ²

AKROMIDĀ® B28 GF 25 9 FR black (8250) - PA6, 25% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, UV stabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.

AKROLOYĀ®

UL

PARA GF 50 HU black (8596)

PARA GF50

AKROLOYĀ® PARA GF 50 HU black (8596) - PARA, 50% GF, highed modulus and strength, easy flowing, listed at UL in all colors, metal substitute

Modulus

19.700MPa

Strength

295MPa

Impact

78kJ/mĀ²

AKROLOYĀ® PARA GF 50 HU black (8596) - PARA, 50% GF, highed modulus and strength, easy flowing, listed at UL in all colors, metal substitute

AKROMIDĀ®

B3 GF 30 9 black (8643)

PA6 GF30

AKROMIDĀ® B3 GF 30 9 black (8643) - 30% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

10.000MPa

Strength

150MPa

Impact

55kJ/mĀ²

AKROMIDĀ® B3 GF 30 9 black (8643) - 30% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROLOYĀ®

UL

PARA GF 60 HU black (8519)

PARA GF60

AKROLOYĀ® PARA GF 60 HU black (8519) - PARA, 60% GF, high modulus and strength, easy flowing, listed at UL in all colors, metal substitute

Modulus

24.000MPa

Strength

310MPa

Impact

80kJ/mĀ²

AKROLOYĀ® PARA GF 60 HU black (8519) - PARA, 60% GF, high modulus and strength, easy flowing, listed at UL in all colors, metal substitute

145680

PRECITEĀ®

Preliminary

P3 GF 50 black (6925)PBT GF 50

PRECITEĀ® P3 GF 50 black (6925) is a 50% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.

Properties

Modulus

17.000MPa

Strength

175MPa

Impact

60kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
17000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
175 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
1,9 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
16500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
285 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
60 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
12 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
215 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
225 Ā°C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
725 Ā°C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,71 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
0,2 %

Water absorption

ISO 62

23Ā°C, saturated
0,4 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Electrical Properties

Dielectric strength

IEC 60243

3 mm
425 kV/mm

Rheological Properties

MVR

ISO 1133

250Ā°C/2,16kg
2 cmĀ³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more