B28 GM 10/20 6 black (8640)PA6 (GF10+GB20)

AKROMID® B28 GM 10/20 6 black (8640) is a 10% glass fiber and 20% glass beads reinforced, easy flowing polyamide 6. Due to its good flowability, the material is not only easy to process but also shows good surface properties. Furthermore, the inorganic heat stabilisation as well as the dimensional stability make it the material of your choice for covers and housings in automotive interior applications.

Features

heat stabilised 160
low warpage
easy flow

Properties

Modulus

5.500MPa

Strength

100MPa

Impact

50kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
5500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
100 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
3,2 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
50 kJ/m²

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
222 °C

Flammability

Flammability

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General Properties

Density

ISO 1183

23°C
1,35 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,3 - 0,5 %
0,6 - 0,8 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.