AKROMID®

B28 GF 30 S3 white (8349)PA6-I GF30

AKROMID® B28 GF 30 S3 white (8349) is a 30% glass fibre reinforced, easy flowing polyamide 6. Furthermore, the material is impact modified and therefore characterised by a higher dry impact strength compared to standard PA 6 GF 30. Its high strength and stiffness make it the material of your choice for technical applications in industrial engineering and in the furniture industry. The material is colored similar to RAL9003.

Features

impact modified

Properties

Modulus

8.900MPa

Strength

150MPa

Impact

94kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
8900 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
150 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
4 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
8200 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
240 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
4,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
94 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
18 kJ/m²

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General Properties

Density

ISO 1183

23°C
1,42 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Rheological Properties

Flowability

AKRO

1 mm Thickness
2 mm Thickness
130 mm
450 mm

MVR

ISO 1133

275°C/5kg
31 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Similar products

AKRO Compound Explorer

AKROMID®

B3 GF 30 S1 white (3767)

PA6-I GF30

AKROMID® B3 GF 30 S1 white (3767) is a 30% glass fiber reinforced, impact modified Polyamide 6 in white color, similar to RAL 9010. It is characterised by high stiffness and strength as well as a higher notched impact strength compared to a standard

Modulus

9.000MPa

Strength

160MPa

Impact

105kJ/m²

AKROMID®

B3 GF 30 S1 natural (1383)

PA6-I GF30

AKROMID® B3 GF 30 S1 natural (1383) is a 30% glass fiber reinforced, impact modified Polyamide 6. It is characterised by high stiffness and strength as well as a higher impact strength compared to a standard PA 6 GF 30. The material is therefore perf

Modulus

8.000MPa

Strength

125MPa

Impact

110kJ/m²

AKROMID®

B3 GF 30 S1 black (2091)

PA6-I GF30

AKROMID® B3 GF 30 S1 black (2091) is a 30% glass fiber reinforced, impact modified Polyamide 6. It is characterised by high stiffness and strength as well as a higher impact strength compared to a standard PA 6 GF 30. The material is therefore perfec

Modulus

7.500MPa

Strength

125MPa

Impact

110kJ/m²

AKROMID®

B3 GF 30 S1 LA black (4446)

PA6-I GF30

AKROMID® B3 GF 30 S1 LA black (4446) is a 30% glass fiber reinforced, impact modified Polyamide 6. It is characterised by a medium impact strength as well as a high stiffness and strength. Furthermore, the material impresses with its laser markabilit

Modulus

8.400MPa

Strength

150MPa

Impact

110kJ/m²

AKROMID®

B3 GF 30 2 S1 grey (4289)

PA6-I GF30

AKROMID® B3 GF 30 2 S1 grey (4289) is a 30% glass fiber reinforced, impact modified Polyamide 6 in grey (similar to RAL 7024). It is characterised by high stiffness and strength as well as a higher impact strength compared to a standard PA 6 GF 30. F

Modulus

8.500MPa

Strength

120MPa

Impact

65kJ/m²

AKROMID®

B3 GF 30 S1 LA black (7704)

PA6-I GF30

AKROMID® B3 GF 30 S1 LA black (7704) is a 30% glass fiber reinforced, impact modified Polyamide 6. It is characterised by a medium impact strength as well as a high stiffness and strength. Furthermore, the material impresses with its laser markabilit

Modulus

9.000MPa

Strength

150MPa

Impact

95kJ/m²

AKROMID®

UL
Preliminary

B25 GF 30 1 FR white (9012)

PA6 GF30 FR(44)

AKROMID® B25 GF 30 1 FR white (9012) is an UL-listed, flame-retardant, heat-stabilised and 30% glass fibre-reinforced PA6 colored in white, similar to RAL 9016. The material is based on a flame-retardant system that is free of red phosphorus, halogen

Modulus

11.300MPa

Strength

140MPa

Impact

64kJ/m²

AKROMID®

Preliminary

B3 GF 30 1 S1 natural (9150)

PA6-I GF30

AKROMID® B3 GF 30 1 S1 natural (9150) is a 30% glass fiber reinforced, impact modified Polyamide 6. It is characterised by a medium impact strength as well as a high stiffness and strength. Furthermore, the material impresses with very good surface p

Modulus

8.300MPa

Strength

145MPa

Impact

100kJ/m²

AKROMID®

C28 GF 25 FRT natural (7332)

PA-Blend GF25 FR(44)

C28 GF 25 FRT natural (7332) is a 25 % glass fiber reinforced, flame retardant and easy flowing PA blend. The material is based on a flame retardant system that is free of red phosphorus and halogens. This grade is suitable for railroad applications

Modulus

10.800MPa

Strength

157MPa

Impact

64kJ/m²

AKROMID®

B3 GF 50 S1 black (2000)

PA6-I GF50

AKROMID® B3 GF 50 S1 black 950089 (2000) is a 50% glass fiber reinforced, impact modified Polyamide 6. It is characterised by very high stiffness and strength as well as a higher notched impact strength compared to a standard PA 6 GF 50. The material

Modulus

15.000MPa

Strength

190MPa

Impact

100kJ/m²

AKROMID®

B3 GF 15 S3 black (2345)

PA6-I GF15

AKROMID® B3 GF 15 S3 black (2345) is a 15% glass fiber reinforced, impact modified Polyamide 6. It is characterised by medium stiffness and strength as well as a higher impact strength compared to a standard PA 6 GF 15. It also has good surface prope

Modulus

5.500MPa

Strength

110MPa

Impact

75kJ/m²

AKROMID®

B3 GF 25 1 natural (2463)

PA6 GF25

AKROMID® B3 GF 25 1 natural (2463) is a 25% glass fibre reinforced, heat stabilised polyamide 6 with high stiffness and strength and light inherent color

Modulus

8.500MPa

Strength

160MPa

Impact

85kJ/m²