PRECITE^®

P3 S1 black (7522)

PBT I

PRECITE® P3 S1 black (7522) - PBT unreinforced, impact modified, good dimensional stability.

Modulus

1.750MPa

Strength

40MPa

Impact

180kJ/m²

PRECITE® P3 S1 black (7522) - PBT unreinforced, impact modified, good dimensional stability.

AKROMID^®

B3 GF 50 4 RM-M black (3221)

PA6+X GF50

AKROMID® B3 GF 50 4 RM-M black (3221) - 50% glass fiber reinforced PA 6 with good surface properties, chemically stabilised, reduced moisture absorption

Modulus

16.500MPa

Strength

210MPa

Impact

75kJ/m²

AKROMID® B3 GF 50 4 RM-M black (3221) - 50% glass fiber reinforced PA 6 with good surface properties, chemically stabilised, reduced moisture absorption

AKROMID^®

B3 GF 30 1 black (2485)

PA6 GF30

AKROMID® B3 GF 30 1 black (2485) - 30% glass fiber reinforced PA 6, heat stabilised, industrial engineering, automotive, also as biomass-balanced and chemical recycled PA6.

Modulus

10.300MPa

Strength

185MPa

Impact

75kJ/m²

AKROMID® B3 GF 30 1 black (2485) - 30% glass fiber reinforced PA 6, heat stabilised, industrial engineering, automotive, also as biomass-balanced and chemical recycled PA6.

AKROMID^®

B3 GF 50 1 black (20008)

PA6 GF50

AKROMID® B3 GF 50 black (20008) - 50% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

17.000MPa

Strength

210MPa

Impact

100kJ/m²

AKROMID® B3 GF 50 black (20008) - 50% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID^®

Preliminary

B28 GF 35 9 FR black (8189)

PA6 GF35 FR(40)

AKROMID® B28 GF 35 9 FR black (8189) - PA6, 35% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.

Modulus

12.600MPa

Strength

152MPa

Impact

70kJ/m²

AKROMID® B28 GF 35 9 FR black (8189) - PA6, 35% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.

AKROMID^®

Preliminary

B28 GF 25 9 FR black (8250)

PA6 GF25 FR(40)

AKROMID® B28 GF 25 9 FR black (8250) - PA6, 25% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, UV stabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.

Modulus

9.000MPa

Strength

135MPa

Impact

81kJ/m²

AKROMID® B28 GF 25 9 FR black (8250) - PA6, 25% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, UV stabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.

AKROMID^®

B28 GM 10/20 1 LA black (4790)

PA6 (GF10+GB20)

AKROMID® B28 GM 10/20 1 LA black (4790) - PA6, 10% glass fibre, 20% glass bead, heat stabilised, laser markable, easy flowing, good surface, reduced warpage.

Modulus

5.700MPa

Strength

110MPa

Impact

30kJ/m²

AKROMID® B28 GM 10/20 1 LA black (4790) - PA6, 10% glass fibre, 20% glass bead, heat stabilised, laser markable, easy flowing, good surface, reduced warpage.

1 4 5 680

AKROMID^®

A3 ICF 40 black (5116)PA66 CF40

AKROMID® A3 ICF 40 black (5116) is a 40% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties

Properties

Modulus

33.000MPa

Strength

270MPa

Impact

60kJ/m²

Sustainability

Recycled content

40 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.

1 mm/min | conditioned

33000 MPa

20000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.

5 mm/min | conditioned

270 MPa

200 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.

5 mm/min | conditioned

1,5 %

2,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.

2 mm/min | conditioned

30000 MPa

22000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.

2 mm/min | conditioned

370 MPa

300 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.

2 mm/min | conditioned

1,8 %

2,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.

23°C | conditioned

30°C | d.a.m.

60 kJ/m²

70 kJ/m²

55 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.

23°C | conditioned

30°C | d.a.m.

9 kJ/m²

12 kJ/m²

7 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa

255 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa

265 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa

235 °C

Melting temperature

ISO 11357-3

DSC, 10K/min

262 °C

Coefficient of linear thermal expansion

ISO 11359-1/2

23°C to 80°C | parallel

23°C to 80°C | transverse

0,04 10⁻⁴/K

0,78 10⁻⁴/K

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h

20.000 h

155 °C

130 °C

Thermal conductivity

DIN 52612

0,47 W/mK

Flammability

Burning rate

UL 94

1,6 mm Wall thickness

HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness

General properties

Density

ISO 1183

23°C

1,34 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.

1,5 %

Molding shrinkage

ISO 294-4

flow

transverse

0,1 - 0,3 %

0,4 - 0,6 %

Electrical Properties

Surface resistivity

DIN EN 62631-3-2

d.a.m.

conditioned

10³ Ω

Rheological Properties

Flowability

AKRO

2 mm Thickness

360 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Find the right compound

A3 ICF 40 black (5116)PA66 CF40

Sustainability

Recycled content

Mechanical Properties

Tensile modulus

Tensile stress at break

Tensile strain at break

Flexural modulus

Flexural strength

Flexural strain at break

Charpy impact strength

Charpy notched impact strength

Thermal Properties

Temperature of deflection under load HDT/A

Temperature of deflection under load HDT/B

Temperature of deflection under load HDT/C

Melting temperature

Coefficient of linear thermal expansion

Temperature index for 50% loss of tensile strength

Thermal conductivity

Flammability

Burning rate

Burning rate (<100 mm/min)

General properties

Density

Humidity absorption

Molding shrinkage

Electrical Properties

Surface resistivity

Rheological Properties

Flowability

Do you have any questions? We are happy to help.

Find the right compound

A3 ICF 40 black (5116).css-117ixes{line-height:1.5;display:block;margin-top:var(--chakra-space-2);font-weight:var(--chakra-fontWeights-normal);font-size:var(--chakra-fontSizes-sm);color:var(--chakra-colors-kisPrimaryTextLight-700);}PA66 CF40

Sustainability

Recycled content

Mechanical Properties

Tensile modulus

Tensile stress at break

Tensile strain at break

Flexural modulus

Flexural strength

Flexural strain at break

Charpy impact strength

Charpy notched impact strength

Thermal Properties

Temperature of deflection under load HDT/A

Temperature of deflection under load HDT/B

Temperature of deflection under load HDT/C

Melting temperature

Coefficient of linear thermal expansion

Temperature index for 50% loss of tensile strength

Thermal conductivity

Flammability

Burning rate

Burning rate (<100 mm/min)

General properties

Density

Humidity absorption

Molding shrinkage

Electrical Properties

Surface resistivity

Rheological Properties

Flowability

Do you have any questions? We are happy to help.

A3 ICF 40 black (5116)PA66 CF40