HEADER Granulat 1920x700

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/m²
558 Compounds found
Recommended  
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

PRECITE®

P3 S1 black (7522)

PBT I

PRECITE® P3 S1 black (7522) - PBT unreinforced, impact modified, good dimensional stability.

Modulus

1.750MPa

Strength

40MPa

Impact

180kJ/m²

PRECITE® P3 S1 black (7522) - PBT unreinforced, impact modified, good dimensional stability.

AKROMID®

B3 GF 50 4 RM-M black (3221)

PA6+X GF50

AKROMID® B3 GF 50 4 RM-M black (3221) - 50% glass fiber reinforced PA 6 with good surface properties, chemically stabilised, reduced moisture absorption

Modulus

16.500MPa

Strength

210MPa

Impact

75kJ/m²

AKROMID® B3 GF 50 4 RM-M black (3221) - 50% glass fiber reinforced PA 6 with good surface properties, chemically stabilised, reduced moisture absorption

AKROMID®

B3 GF 30 1 black (2485)

PA6 GF30

AKROMID® B3 GF 30 1 black (2485) - 30% glass fiber reinforced PA 6, heat stabilised, industrial engineering, automotive, also as biomass-balanced and chemical recycled PA6.

Modulus

10.300MPa

Strength

185MPa

Impact

75kJ/m²

AKROMID® B3 GF 30 1 black (2485) - 30% glass fiber reinforced PA 6, heat stabilised, industrial engineering, automotive, also as biomass-balanced and chemical recycled PA6.

AKROMID®

B3 GF 50 1 black (20008)

PA6 GF50

AKROMID® B3 GF 50 black (20008) - 50% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

17.000MPa

Strength

210MPa

Impact

100kJ/m²

AKROMID® B3 GF 50 black (20008) - 50% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

UL
Preliminary

B28 GF 35 9 FR black (8189)

PA6 GF35 FR(40)

AKROMID® B28 GF 35 9 FR black (8189) - PA6, 35% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.

Modulus

12.600MPa

Strength

152MPa

Impact

70kJ/m²

AKROMID® B28 GF 35 9 FR black (8189) - PA6, 35% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.

AKROMID®

UL
Preliminary

B28 GF 25 9 FR black (8250)

PA6 GF25 FR(40)

AKROMID® B28 GF 25 9 FR black (8250) - PA6, 25% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, UV stabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.

Modulus

9.000MPa

Strength

135MPa

Impact

81kJ/m²

AKROMID® B28 GF 25 9 FR black (8250) - PA6, 25% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, UV stabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.

AKROMID®

B28 GM 10/20 1 LA black (4790)

PA6 (GF10+GB20)

AKROMID® B28 GM 10/20 1 LA black (4790) - PA6, 10% glass fibre, 20% glass bead, heat stabilised, laser markable, easy flowing, good surface, reduced warpage.

Modulus

5.700MPa

Strength

110MPa

Impact

30kJ/m²

AKROMID® B28 GM 10/20 1 LA black (4790) - PA6, 10% glass fibre, 20% glass bead, heat stabilised, laser markable, easy flowing, good surface, reduced warpage.

145680

AKROMID®

B3 GF 30 S1 black (1281)PA6-I GF30

AKROMID® B3 GF 30 S1 black (1281) is a 30% glass fiber reinforced, impact modified Polyamide 6. It is characterised by high stiffness and strength as well as a higher impact strength compared to a standard PA 6 GF 30. The material is therefore perfectly suitable for industrial applications and for housings and covers in the automotive industry.

Features

impact modified

Properties

Modulus

8.800MPa

Strength

150MPa

Impact

85kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
8800 MPa
5500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
150 MPa
90 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,5 %
6 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
8300 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
85 kJ/m²
100 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
15 kJ/m²
20 kJ/m²
10 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
190 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
222 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,35 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Rheological Properties

MVR

ISO 1133

275°C/5kg
25 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.