AKROMID®

B3 GF 30 S1 LA black (4446)

PA6-I GF30

AKROMID® B3 GF 30 S1 LA black (4446) - PA 6, 30% glass fiber reinforced, impact modified, laser markable, housings, covers, automotive

Modulus

8.400MPa

Strength

150MPa

Impact

110kJ/m²

AKROMID® B3 GF 30 S1 LA black (4446) - PA 6, 30% glass fiber reinforced, impact modified, laser markable, housings, covers, automotive

AKROMID®

B28 LGF 40 1 L black (6155)

PA6 + PP LGF40

AKROMID® B28 LGF 40 1 L black (6155) - PA6/PP-Blend, 40% long glass fiber reinforced, easy flowing, lightweight, low shrinkage, very good fatigue performance

Modulus

12.000MPa

Strength

200MPa

Impact

100kJ/m²

AKROMID® B28 LGF 40 1 L black (6155) - PA6/PP-Blend, 40% long glass fiber reinforced, easy flowing, lightweight, low shrinkage, very good fatigue performance

AKROMID®

A3 GF 50 6 natural (5916)

PA66 GF50

AKROMID® A3 GF 50 6 natural (5916) - 50% glass fiber reinforced PA 6.6, inorganically high heat stabilised, optimized for extrusion, technical parts in industrial engineering and automotive industry

Modulus

17.000MPa

Strength

270MPa

Impact

105kJ/m²

AKROMID® A3 GF 50 6 natural (5916) - 50% glass fiber reinforced PA 6.6, inorganically high heat stabilised, optimized for extrusion, technical parts in industrial engineering and automotive industry

AKROMID®

C3 GF 35 5 XTC black (6680)

PA66+PA6 GF35

AKROMID® C3 GF 35 5 XTC black (6680) - PA6.6/6 blend, 35% glass fiber reinforced, high heat stabilised, industrial engineering, automotive industry, laser marking

Modulus

11.500MPa

Strength

200MPa

Impact

105kJ/m²

AKROMID® C3 GF 35 5 XTC black (6680) - PA6.6/6 blend, 35% glass fiber reinforced, high heat stabilised, industrial engineering, automotive industry, laser marking

PRECITE®

Preliminary

P3 GF 50 black (6925)

PBT GF 50

PRECITE® P3 GF 50 black (6925) is a 50% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.

Modulus

17.000MPa

Strength

175MPa

Impact

60kJ/m²

PRECITE® P3 GF 50 black (6925) is a 50% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.

AKROMID®

B3 GF 30 1 black (20000)

PA6 GF30

AKROMID® B3 GF 30 1 black (20000) - 30% glass fiber reinforced PA 6, heat stabilised for technical parts in industrial engineering, automotive and agricultural machinery industry

Modulus

9.500MPa

Strength

175MPa

Impact

90kJ/m²

AKROMID® B3 GF 30 1 black (20000) - 30% glass fiber reinforced PA 6, heat stabilised for technical parts in industrial engineering, automotive and agricultural machinery industry

PRECITE®

Preliminary

E ICF 30 black (7429)

PET CF30

PRECITE® E ICF 30 black (7429) - PET, 30% recycled carbon fibre , very high stiffness and toughness, improved surface finish, good dimensionstability, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.

Modulus

24.000MPa

Strength

220MPa

Impact

44kJ/m²

PRECITE® E ICF 30 black (7429) - PET, 30% recycled carbon fibre , very high stiffness and toughness, improved surface finish, good dimensionstability, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.

117181980

AKROMID®

A3 GK 30 natural (3689)PA66 GB30

AKROMID® A3 GK 30 natural (3689) is a PA 6.6 filled with 30% glass beads. It is characterized by a high surface quality and low tendency to warp, which makes it suitable for use in technically demanding components in mechanical engineering and in the automotive industry.

Features

recycled content
low warpage

Properties

Modulus

5.000MPa

Strength

90MPa

Impact

28kJ/m²

Sustainability

Recycled content

30 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
5000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
90 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
4 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
4300 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
140 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
6,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
30°C | d.a.m.
-
28 kJ/m²
22 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
30°C | d.a.m.
-
4 kJ/m²
3 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
100 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
225 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
650 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,35 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,0 %

Molding shrinkage

ISO 294-4

flow
transverse
1,1 %
1,3 %

Electrical Properties

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1013 Ω

Comparative tracking index

IEC 60112

Test liquid A
500 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more