PRECITE®

Preliminary

P3 black (7811)

PBT

PRECITE® P3 black (7811) - PBT, unreinforced, medium viscosity, good dimensional stability, automotive, E&E, appliances industries.

Modulus

2.600MPa

Strength

60MPa

Impact

90kJ/m²

PRECITE® P3 black (7811) - PBT, unreinforced, medium viscosity, good dimensional stability, automotive, E&E, appliances industries.

AKROMID®

C3 GF 30 1 black (4363)

PA66+PA6 GF30

AKROMID® C3 GF 30 1 black (4363) - PA6.6/6 blend, 30% glass fiber reinforced, heat stabilised, industrial engineering, automotive industry

Modulus

9.300MPa

Strength

185MPa

Impact

75kJ/m²

AKROMID® C3 GF 30 1 black (4363) - PA6.6/6 blend, 30% glass fiber reinforced, heat stabilised, industrial engineering, automotive industry

AKROLOY®

PA ICF 30 black (5269)

PA66+PA6I/6T CF30

AKROLOY® PA ICF 30 black (5269) is a 30% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.

Modulus

25.000MPa

Strength

220MPa

Impact

50kJ/m²

AKROLOY® PA ICF 30 black (5269) is a 30% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.

AKROMID®

B3 GF 60 4 RM-M black (5238)

PA6+X GF60

AKROMID® B3 GF 60 4 RM-M black (5238) is a 60% glass fibre reinforced, chemical stabilised polyamide 6 with low humidity absorption and very good surface finish.

Modulus

22.500MPa

Strength

225MPa

Impact

60kJ/m²

AKROMID® B3 GF 60 4 RM-M black (5238) is a 60% glass fibre reinforced, chemical stabilised polyamide 6 with low humidity absorption and very good surface finish.

AKROMID®

C3 GF 35 5 XTC black (5552)

PA66+PA6 GF35

AKROMID® C3 GF 35 5 XTC black (5552) is a 35% glass fibre reinforced, high heat stabilised polyamid 66/6 blend with high stiffness and strength and with extra high temperature tolerance.

Modulus

11.000MPa

Strength

200MPa

Impact

100kJ/m²

AKROMID® C3 GF 35 5 XTC black (5552) is a 35% glass fibre reinforced, high heat stabilised polyamid 66/6 blend with high stiffness and strength and with extra high temperature tolerance.

AKROMID®

B28 LGF 40 1 L black (6155)

PA6 + PP LGF40

AKROMID® B28 LGF 40 1 L black (6155) - PA6/PP-Blend, 40% long glass fiber reinforced, easy flowing, lightweight, low shrinkage, very good fatigue performance

Modulus

12.000MPa

Strength

200MPa

Impact

100kJ/m²

AKROMID® B28 LGF 40 1 L black (6155) - PA6/PP-Blend, 40% long glass fiber reinforced, easy flowing, lightweight, low shrinkage, very good fatigue performance

AKROMID®

B28 GF 33 1 GIT black (6846)

PA6 GF33

AKROMID® B28 GF 33 1 GIT black (6846) - 33% glass fibre reinforced, polyamide 6, heat stabilised, easy flowing, gas injection technology.

Modulus

10.500MPa

Strength

190MPa

Impact

95kJ/m²

AKROMID® B28 GF 33 1 GIT black (6846) - 33% glass fibre reinforced, polyamide 6, heat stabilised, easy flowing, gas injection technology.

117181979

AKROLOY®

UL

PA GF 60 7 natural (2941)PA66+PA6I/6T GF60

AKROLOY® PA GF 60 7 natural (2941) is a 60% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state. The advanced version of this Product is AKROLOY® PA GF 60 natural (6465) with a modern stabilization technology, featuring improved weld-line strength and an even wider process window. UL listed.

Regulatory

ul

Properties

Modulus

21.000MPa

Strength

275MPa

Impact

100kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
21000 MPa
20000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
275 MPa
245 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,5 %
2,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
20000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
405 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
100 kJ/m²
95 kJ/m²
90 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
16 kJ/m²
16 kJ/m²
14 kJ/m²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.
330 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
225 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
245 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
255 °C

Coefficient of linear thermal expansion

ISO 11359-1/2

23°C to 80°C | parallel
23°C to 80°C | transverse
0,15 10⁻⁴/K
0,55 10⁻⁴/K

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
140 - 150 °C
110 - 130 °C

Flammability

Burning rate

UL 94

UL
0,8 mm Wall thickness
HB Class

GWIT

IEC 60695-2-13

0,8 mm Wall thickness
650 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,72 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,8 %

Water absorption

ISO 62

23°C, saturated
3 - 3,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0,0 - 0,2 %
0,2 - 0,4 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more