HEADER Granulat 1920x700

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/m²
558 Compounds found
Recommended  
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMID®

UL

A3 GF 50 HU grey (6601)

PA66 GF50

AKROMID® A3 GF 50 HU grey (6601) - 50% glass fiber reinforced PA 6.6, heat stabilised, listed at UL in all colors, technical parts in industrial engineering and automotive industry

Modulus

17.000MPa

Strength

255MPa

Impact

110kJ/m²

AKROMID® A3 GF 50 HU grey (6601) - 50% glass fiber reinforced PA 6.6, heat stabilised, listed at UL in all colors, technical parts in industrial engineering and automotive industry

AKROMID®

B28 GF 15 2 black (7060)

PA6 GF15

AKROMID® B28 GF 15 2 black (7060) - 15% glass fibre reinforced, heat- and UV-stabilised, easy flowing polyamide 6, average stiffness and strength, passes ISO 4892-2 with 1200h exposure time.

Modulus

6.100MPa

Strength

108MPa

Impact

32kJ/m²

AKROMID® B28 GF 15 2 black (7060) - 15% glass fibre reinforced, heat- and UV-stabilised, easy flowing polyamide 6, average stiffness and strength, passes ISO 4892-2 with 1200h exposure time.

AKROMID®

Preliminary

B3 GFM 20/30 1 black (7677)

PA6 (GF20+MD30)

AKROMID® B3 GFM 20/30 1 black (7677) is a 20% glass fibre reinforced and 30% mineral filled, heat stabilised polyamide 6 with good surface and dimensional stability.

Modulus

14.000MPa

Strength

145MPa

Impact

45kJ/m²

AKROMID® B3 GFM 20/30 1 black (7677) is a 20% glass fibre reinforced and 30% mineral filled, heat stabilised polyamide 6 with good surface and dimensional stability.

AKROMID®

A3 GF 35 2 black (21010)

PA66 GF35

AKROMID® A3 GF 35 2 black (21010) is a 35% glass fibre reinforced, UV-stabilised polyamide 6.6 with high stiffness and strength

Modulus

12.000MPa

Strength

185MPa

Impact

50kJ/m²

AKROMID® A3 GF 35 2 black (21010) is a 35% glass fibre reinforced, UV-stabilised polyamide 6.6 with high stiffness and strength

AKROMID®

B3 ICF 30 AM black (7451)

PA6 CF30

AKROMID® B3 ICF 30 AM black (7451) is a 30% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties as well as optimised viscosity. It is suitable for a stable additive manufacturing process (3D Printing) at fast production speeds.

Modulus

20.000MPa

Strength

190MPa

Impact

45kJ/m²

AKROMID® B3 ICF 30 AM black (7451) is a 30% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties as well as optimised viscosity. It is suitable for a stable additive manufacturing process (3D Printing) at fast production speeds.

AKROMID®

Preliminary

NEXT B3 GF 30 1 L CR natural (8312)

PA6 + PP GF30

AKROMID® NEXT B3 GF 30 1 L CR natural (8312) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.

Modulus

8.800MPa

Strength

140MPa

Impact

70kJ/m²

AKROMID® NEXT B3 GF 30 1 L CR natural (8312) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.

AKROMID®

B3 GF 15 1 L black (4670)

PA6+PP GF15

AKROMID® B3 GF 15 1 L black (4670) - PA6/PP-Blend 15% glass fibre reinforced, lower density, cost reduced, calcium chloride

Modulus

5.200MPa

Strength

105MPa

Impact

60kJ/m²

AKROMID® B3 GF 15 1 L black (4670) - PA6/PP-Blend 15% glass fibre reinforced, lower density, cost reduced, calcium chloride

116171880

PRECITE®

P1 natural (7010)PBT

PRECITE® P1 natural (7010) an unreinforced polybutylene terephthalate (PBT) with low viscosity and good dimensional stability. It is particularly suitable for precision parts in the automotive, E&E or appliances industries.

Features

reduced moisture
easy flow
E&E
Sports & leisure

Properties

Modulus

2.400MPa

Strength

55MPa

Impact

180kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
2400 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
55 MPa

Tensile strain at yield

ISO 527-2

50 mm/min | d.a.m.
10 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2600 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
90 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
3,5 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
55 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
223 °C

Flammability

Burning rate 5V

UL 94

0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,31 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,2 %

Water absorption

ISO 62

23°C, saturated
0,5 %

Molding shrinkage

ISO 294-4

flow
transverse
1,7 - 1,9 %
1,8 - 2,0 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
> 1013 Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1012 Ω

Rheological Properties

MVR

ISO 1133

250°C/2,16kg
65 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more