AKROMID®
AKROMID® A3 GF 35 1 HU natural (8418) is a 35% glass fibre reinforced, heat ageing resistant polyamide 6.6 with high rigidity and strength. This UL94 HB listed grade is suitable for technical components in mechanical engineering and the automotive industry.
Features
Regulatory
Properties
11.900MPa
216MPa
Na
ISO 527-2
ISO 527-2
ISO 527-2
ISO 11357-3
UL 94
ISO 1183
ISO 1110
ISO 294-4
IEC 60112
ASTM D3638
Discover all the technical specifications at a single glance here.
The values mentioned are recommendations. We only recommend desiccant / dry air dryers or vacuum dryers. Too long a drying time and the resulting residual moisture content below the lower limit can lead to filling problems and surface defects. The specified drying time refers to closed and undamaged bagged material. When processing from previously opened bags or from octabins with polyolefin inliners, a longer drying time may be necessary. It is recommended to check the residual moisture content after the drying process.
Drying time
0 - 4 h
Drying temperature (τ ≤ -30°C)
80 °C
Processing moisture
0,02 - 0,1 %
Feed section
60 - 80 °C
Temperature Zone 1 - Zone 4
260 - 300 °C
Nozzle temperature
270 - 310 °C
Melt temperature
280 - 300 °C
Mold temperature
80 - 100 °C
Holding pressure, spec.
300 - 800 bar
Back pressure, spec.
50 - 150 bar
Injection speed
medium to high
Screw speed
8 - 15 m/min
Explore more exciting application examples that illustrate how our products can be beneficial to you in various situations and industries.
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.