HEADER Granulat 1920x700

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/mĀ²
558 Compounds found
Recommended Ā 
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

PRECITEĀ®

Preliminary

P3 GK 30 natural (7643)

PBT GK30

PRECITEĀ® P3 GK 30 natural (7643) is a 30% glass bead filled poly(butylene terephthalate) (PBT) with excellent dimensional stability, low warpage and high surface quality.

Modulus

3.900MPa

Strength

50MPa

Impact

25kJ/mĀ²

PRECITEĀ® P3 GK 30 natural (7643) is a 30% glass bead filled poly(butylene terephthalate) (PBT) with excellent dimensional stability, low warpage and high surface quality.

AKROMIDĀ®

Preliminary

T5 GF 35 6 black (8004)

PPA GF35

AKROMIDĀ® T5 GF 35 6 black (8004) is a 35% glass fibre reinforced, inorganic high temperature stabilised polyphthalamide with high rigidity and strength, as well as high temperature and chemical resistance

Modulus

12.500MPa

Strength

230MPa

Impact

70kJ/mĀ²

AKROMIDĀ® T5 GF 35 6 black (8004) is a 35% glass fibre reinforced, inorganic high temperature stabilised polyphthalamide with high rigidity and strength, as well as high temperature and chemical resistance

PRECITEĀ®

Preliminary

P3 black (7811)

PBT

PRECITEĀ® P3 black (7811) - PBT, unreinforced, medium viscosity, good dimensional stability, automotive, E&E, appliances industries.

Modulus

2.600MPa

Strength

60MPa

Impact

90kJ/mĀ²

PRECITEĀ® P3 black (7811) - PBT, unreinforced, medium viscosity, good dimensional stability, automotive, E&E, appliances industries.

PRECITEĀ®

Preliminary

P3 ICF 15 black (7720)

PBT CF 15

PRECITEĀ® P3 ICF 15 black (7720)- PBT, 15% recycled carbon fibre , medium stiffness and toughness, improved surface finish, good dimensionstability, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.

Modulus

12.500MPa

Strength

135MPa

Impact

50kJ/mĀ²

PRECITEĀ® P3 ICF 15 black (7720)- PBT, 15% recycled carbon fibre , medium stiffness and toughness, improved surface finish, good dimensionstability, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.

PRECITEĀ®

P1 natural (7010)

PBT

PRECITEĀ® P1 natural (7010) - PBT, unreinforced, low viscosity, good dimensional stability, automotive, E&E, appliances industries.

Modulus

2.400MPa

Strength

55MPa

Impact

180kJ/mĀ²

PRECITEĀ® P1 natural (7010) - PBT, unreinforced, low viscosity, good dimensional stability, automotive, E&E, appliances industries.

AKROMIDĀ®

Preliminary

B3 GFM 20/30 1 black (7677)

PA6 (GF20+MD30)

AKROMIDĀ® B3 GFM 20/30 1 black (7677) is a 20% glass fibre reinforced and 30% mineral filled, heat stabilised polyamide 6 with good surface and dimensional stability.

Modulus

14.000MPa

Strength

145MPa

Impact

45kJ/mĀ²

AKROMIDĀ® B3 GFM 20/30 1 black (7677) is a 20% glass fibre reinforced and 30% mineral filled, heat stabilised polyamide 6 with good surface and dimensional stability.

PRECITEĀ®

Preliminary

P3 GK 20 natural (7642)

PBT GB20

PRECITEĀ® P3 GK 20 natural (7642) is a 20% glass bead filled poly(butylene terephthalate) (PBT) with excellent dimensional stability, low warpage and high surface quality.

Modulus

3.500MPa

Strength

50MPa

Impact

25kJ/mĀ²

PRECITEĀ® P3 GK 20 natural (7642) is a 20% glass bead filled poly(butylene terephthalate) (PBT) with excellent dimensional stability, low warpage and high surface quality.

116171880

AKROMIDĀ®

B3 GF 50 black (4907)PA6 GF50

AKROMIDĀ® B3 GF 50 black (4907) is a 50% glass fibre reinforced high-flow polyamide 6 with very high rigidity and strength. The material is suitable for technical components in mechanical engineering, automotive industry as well as construction industry.

Features

easy flow

Properties

Modulus

17.000MPa

Strength

240MPa

Impact

100kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
17000 MPa
11000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
240 MPa
160 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3 %
5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
16000 MPa
11000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
360 MPa
250 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
100 kJ/mĀ²
105 kJ/mĀ²
90 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
20 kJ/mĀ²
23 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
220 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 Ā°C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
185 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 Ā°C

Coefficient of linear thermal expansion

ISO 11359-1/2

23Ā°C to 80Ā°C | parallel
23Ā°C to 80Ā°C | transverse
0,11 10ā»ā“/K
0,94 10ā»ā“/K

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
150 - 165 Ā°C
120 - 140 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
650 Ā°C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,56 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,3 - 1,6 %

Water absorption

ISO 62

23Ā°C, saturated
4,5 - 5,1 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,4 - 0,6 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
1013 ā„¦ x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1012 ā„¦

Comparative tracking index

IEC 60112

Test liquid A
550 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.