HEADER Granulat 1920x700

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/m²
558 Compounds found
Recommended  
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMID®

B3 ICF 15 black (5026)

PA6 CF15

AKROMID® B3 ICF 15 black (5026) is a 15% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties.

Modulus

11.000MPa

Strength

140MPa

Impact

55kJ/m²

AKROMID® B3 ICF 15 black (5026) is a 15% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties.

AKROMID®

C3 GF 30 1 black (4363)

PA66+PA6 GF30

AKROMID® C3 GF 30 1 black (4363) - PA6.6/6 blend, 30% glass fiber reinforced, heat stabilised, industrial engineering, automotive industry

Modulus

9.300MPa

Strength

185MPa

Impact

75kJ/m²

AKROMID® C3 GF 30 1 black (4363) - PA6.6/6 blend, 30% glass fiber reinforced, heat stabilised, industrial engineering, automotive industry

AKROMID®

B28 GF 30 9 natural (6614)

PA6 GF30

AKROMID® B28 GF 30 9 natural (6614) - PA 6, 30% glassfiber reinforced, easy flow, good surface, technical parts in industrial engineering and automotive industry

Modulus

10.300MPa

Strength

185MPa

Impact

95kJ/m²

AKROMID® B28 GF 30 9 natural (6614) - PA 6, 30% glassfiber reinforced, easy flow, good surface, technical parts in industrial engineering and automotive industry

AKROMID®

A3 GF 30 4 6 black (13690)

PA66 GF30

AKROMID® A3 GF 30 4 6 black (13690) - PA6.6, 30% glass fiber, cooling water, hydrolysis resistant, DPPD free

Modulus

10.000MPa

Strength

190MPa

Impact

85kJ/m²

AKROMID® A3 GF 30 4 6 black (13690) - PA6.6, 30% glass fiber, cooling water, hydrolysis resistant, DPPD free

PRECITE®

Preliminary

P3 GK 20 natural (7642)

PBT GB20

PRECITE® P3 GK 20 natural (7642) is a 20% glass bead filled poly(butylene terephthalate) (PBT) with excellent dimensional stability, low warpage and high surface quality.

Modulus

3.500MPa

Strength

50MPa

Impact

25kJ/m²

PRECITE® P3 GK 20 natural (7642) is a 20% glass bead filled poly(butylene terephthalate) (PBT) with excellent dimensional stability, low warpage and high surface quality.

PRECITE®

Preliminary

E ICF 30 black (7429)

PET CF30

PRECITE® E ICF 30 black (7429) - PET, 30% recycled carbon fibre , very high stiffness and toughness, improved surface finish, good dimensionstability, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.

Modulus

24.000MPa

Strength

220MPa

Impact

44kJ/m²

PRECITE® E ICF 30 black (7429) - PET, 30% recycled carbon fibre , very high stiffness and toughness, improved surface finish, good dimensionstability, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.

PRECITE®

Preliminary

V GF 20 2 natural (7737)

PBT-ASA- GF 20

PRECITE V GF 20 2 natural (7737) is a 20% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.

Modulus

6.500MPa

Strength

110MPa

Impact

50kJ/m²

PRECITE V GF 20 2 natural (7737) is a 20% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.

116171880

AKROMID®

C3 GF 60 1 black (4659)PA66 + PA6 GF60

AKROMID® C3 GF 60 1 black (4659) is a 60% glass fibre reinforced, heat stabilised polyamide 6.6/6 - Blend.

Features

heat stabilised 130

Properties

Modulus

21.300MPa

Strength

270MPa

Impact

96kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
21300 MPa
13200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
270 MPa
180 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,3 %
4 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
22500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
425 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
96 kJ/m²
103 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
19 kJ/m²
24 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
255 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
212 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
260 °C

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
160 - 175 °C
130 - 150 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,71 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,1 %

Molding shrinkage

ISO 294-4

flow
transverse
0,4 %
0,8 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
conditioned
1013 Ω x cm
1010 Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
1012 Ω
1010 Ω

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.