PRECITEĀ®

Preliminary

P1 GF 30 natural (7062)

PBT GF30

PRECITEĀ® P1 GF 30 natural (7062) is a 30% glass fibre reinforced, low viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

Modulus

9.800MPa

Strength

150MPa

Impact

75kJ/mĀ²

PRECITEĀ® P1 GF 30 natural (7062) is a 30% glass fibre reinforced, low viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

PRECITEĀ®

Preliminary

E GF 45 natural (7305)

PET GF 45

PRECITEĀ® E GF 45 natural (7305)- PET, 45% glass fibre, very high stiffness, very high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

16.500MPa

Strength

200MPa

Impact

65kJ/mĀ²

PRECITEĀ® E GF 45 natural (7305)- PET, 45% glass fibre, very high stiffness, very high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

PRECITEĀ®

Preliminary

V GF 20 2 black (7738)

PBT-ASA- GF 20

PRECITE V GF 20 2 black (7738) is a 20% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.

Modulus

6.500MPa

Strength

110MPa

Impact

50kJ/mĀ²

PRECITE V GF 20 2 black (7738) is a 20% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.

PRECITEĀ®

Preliminary

V GF 30 2 natural (7722)

PBT-ASA- GF 30

PRECITE V GF 30 2 natural (7722) is a 30% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.

Modulus

9.800MPa

Strength

140MPa

Impact

60kJ/mĀ²

PRECITE V GF 30 2 natural (7722) is a 30% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.

PRECITEĀ®

Preliminary

P3 black (7811)

PBT

PRECITEĀ® P3 black (7811) - PBT, unreinforced, medium viscosity, good dimensional stability, automotive, E&E, appliances industries.

Modulus

2.600MPa

Strength

60MPa

Impact

90kJ/mĀ²

PRECITEĀ® P3 black (7811) - PBT, unreinforced, medium viscosity, good dimensional stability, automotive, E&E, appliances industries.

AKROMIDĀ®

B3 GF 30 1 L black (4365)

PA6+PP GF30

AKROMIDĀ® B3 GF 30 1 L black (4365) - PA6/PP-Blend glass fibre reinforced with lower density, cost reduced, calcium chloride

Modulus

8.800MPa

Strength

140MPa

Impact

60kJ/mĀ²

AKROMIDĀ® B3 GF 30 1 L black (4365) - PA6/PP-Blend glass fibre reinforced with lower density, cost reduced, calcium chloride

AKROMIDĀ®

C3 GF 30 1 black (4363)

PA66+PA6 GF30

AKROMIDĀ® C3 GF 30 1 black (4363) - PA6.6/6 blend, 30% glass fiber reinforced, heat stabilised, industrial engineering, automotive industry

Modulus

9.300MPa

Strength

185MPa

Impact

75kJ/mĀ²

AKROMIDĀ® C3 GF 30 1 black (4363) - PA6.6/6 blend, 30% glass fiber reinforced, heat stabilised, industrial engineering, automotive industry

116171880

AKROMIDĀ®

B3 GF 25 1 L black (4637)PA6+PP GF25

AKROMIDĀ® B3 GF 25 1 L black (4637) is a PA6/PP-blend with reduced density compared to standard PA6 with 25% glass fibre reinforcement. The material is suitable for components with high strength and stiffness where cost and weight reduction are required at the same time. The chemical resistance of AKROMIDĀ® B3 GF 25 1 L black (4637) is particularly superior to calcium chloride (CaClā‚‚).

Features

heat stabilised 130
reduced density

Properties

Modulus

7.500MPa

Strength

135MPa

Impact

68kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
7500 MPa
5600 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
135 MPa
88 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,3 %
4,5 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
30Ā°C | conditioned
-
68 kJ/mĀ²
58 kJ/mĀ²
67 kJ/mĀ²
54 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
30Ā°C | conditioned
-
15 kJ/mĀ²
15 kJ/mĀ²
13 kJ/mĀ²
10 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
198 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
217 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 Ā°C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
750 Ā°C
725 Ā°C
750 Ā°C

GWIT

IEC 60695-2-13

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
775 Ā°C
750 Ā°C
775 Ā°C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,22 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,55 - 0,75 %

Rheological Properties

MVR

ISO 1133

275Ā°C/5kg
10 cmĀ³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more