AKROMID®

T5 GF 40 black (6486)

PPA GF40

AKROMID® T5 GF 40 black (6486) - 40% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

Modulus

14.500MPa

Strength

245MPa

Impact

80kJ/m²

AKROMID® T5 GF 40 black (6486) - 40% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

AKROLOY®

PA GF 60 natural (6465)

PA66+PA6I/6T GF60

AKROLOY® PA GF 60 natural (6465) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

Modulus

21.000MPa

Strength

280MPa

Impact

100kJ/m²

AKROLOY® PA GF 60 natural (6465) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

PRECITE®

Preliminary

P3 natural (7009)

PBT

PRECITE® P3 natural (7009) - PBT, unreinforced, medium viscosity, good dimensional stability, automotive, E&E, appliances industries.

Modulus

2.400MPa

Strength

55MPa

Impact

180kJ/m²

PRECITE® P3 natural (7009) - PBT, unreinforced, medium viscosity, good dimensional stability, automotive, E&E, appliances industries.

PRECITE®

Preliminary

E GF 20 black (7360)

PET GF 20

PRECITE® E GF 20 black (7360) - PET, 20 % glass fibre, good stiffness, good toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

7.800MPa

Strength

NA

Impact

35kJ/m²

PRECITE® E GF 20 black (7360) - PET, 20 % glass fibre, good stiffness, good toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

AKROMID®

A3 1 S3 black (21002)

PA66-I

AKROMID® A3 1 S3 black (21002) - PA66, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E

Modulus

2.300MPa

Strength

60MPa

Impact

180kJ/m²

AKROMID® A3 1 S3 black (21002) - PA66, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E

AKROMID®

B3 GF 30 1 black (20000)

PA6 GF30

AKROMID® B3 GF 30 1 black (20000) - 30% glass fiber reinforced PA 6, heat stabilised for technical parts in industrial engineering, automotive and agricultural machinery industry

Modulus

9.500MPa

Strength

175MPa

Impact

90kJ/m²

AKROMID® B3 GF 30 1 black (20000) - 30% glass fiber reinforced PA 6, heat stabilised for technical parts in industrial engineering, automotive and agricultural machinery industry

AKROMID®

C28 GF 25 FRT grey (7530)

PA-Blend

AKROMID® C28 GF 25 FRT grey (7530) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 000 65 00, Public Transportation EN 45545-2.

Modulus

11.000MPa

Strength

135MPa

Impact

NA

AKROMID® C28 GF 25 FRT grey (7530) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 000 65 00, Public Transportation EN 45545-2.

116171880

AKROMID®

B3 1 L black (4525)PA6+PP

AKROMID® B3 1 L black (4525) is an unreinforced PA6-PP-blend with reduced density compared to standard PA6. The material can be used where weight and cost reduction is required.

Features

heat stabilised 130
reduced density

Properties

Modulus

2.300MPa

Strength

55MPa

Impact

180kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
2300 MPa
1200 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
55 MPa
40 MPa

Tensile strain at yield

ISO 527-2

50 mm/min | d.a.m.
4,5 %

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
> 20 %
> 20 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2200 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
75 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
no break
no break
no break
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
7 kJ/m²
18 kJ/m²
5 kJ/m²

Ball indentation hardness

ISO 2039-1

358N/30s | d.a.m.
112 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
60 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
130 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Coefficient of linear thermal expansion

ISO 11359-1/2

23°C to 80°C | parallel
23°C to 80°C | transverse
0,95 10⁻⁴/K
0,95 10⁻⁴/K

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
750 °C

GWIT

IEC 60695-2-13

0,8 mm Wall thickness
775 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,04 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,8 - 2,0 %

Molding shrinkage

ISO 294-4

flow
transverse
1,0 - 1,2 %
1,1 - 1,3 %

Rheological Properties

Flowability

AKRO

1 mm Thickness
2 mm Thickness
220 mm
660 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more