PRECITEĀ®

Preliminary

P1 GF 30 natural (7062)

PBT GF30

PRECITEĀ® P1 GF 30 natural (7062) is a 30% glass fibre reinforced, low viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

Modulus

9.800MPa

Strength

150MPa

Impact

75kJ/mĀ²

PRECITEĀ® P1 GF 30 natural (7062) is a 30% glass fibre reinforced, low viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

PRECITEĀ®

Preliminary

E GF 45 natural (7305)

PET GF 45

PRECITEĀ® E GF 45 natural (7305)- PET, 45% glass fibre, very high stiffness, very high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

16.500MPa

Strength

200MPa

Impact

65kJ/mĀ²

PRECITEĀ® E GF 45 natural (7305)- PET, 45% glass fibre, very high stiffness, very high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

PRECITEĀ®

Preliminary

V GF 20 2 black (7738)

PBT-ASA- GF 20

PRECITE V GF 20 2 black (7738) is a 20% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.

Modulus

6.500MPa

Strength

110MPa

Impact

50kJ/mĀ²

PRECITE V GF 20 2 black (7738) is a 20% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.

PRECITEĀ®

Preliminary

V GF 30 2 natural (7722)

PBT-ASA- GF 30

PRECITE V GF 30 2 natural (7722) is a 30% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.

Modulus

9.800MPa

Strength

140MPa

Impact

60kJ/mĀ²

PRECITE V GF 30 2 natural (7722) is a 30% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.

PRECITEĀ®

Preliminary

P3 black (7811)

PBT

PRECITEĀ® P3 black (7811) - PBT, unreinforced, medium viscosity, good dimensional stability, automotive, E&E, appliances industries.

Modulus

2.600MPa

Strength

60MPa

Impact

90kJ/mĀ²

PRECITEĀ® P3 black (7811) - PBT, unreinforced, medium viscosity, good dimensional stability, automotive, E&E, appliances industries.

AKROMIDĀ®

B3 GF 30 1 L black (4365)

PA6+PP GF30

AKROMIDĀ® B3 GF 30 1 L black (4365) - PA6/PP-Blend glass fibre reinforced with lower density, cost reduced, calcium chloride

Modulus

8.800MPa

Strength

140MPa

Impact

60kJ/mĀ²

AKROMIDĀ® B3 GF 30 1 L black (4365) - PA6/PP-Blend glass fibre reinforced with lower density, cost reduced, calcium chloride

AKROMIDĀ®

C3 GF 30 1 black (4363)

PA66+PA6 GF30

AKROMIDĀ® C3 GF 30 1 black (4363) - PA6.6/6 blend, 30% glass fiber reinforced, heat stabilised, industrial engineering, automotive industry

Modulus

9.300MPa

Strength

185MPa

Impact

75kJ/mĀ²

AKROMIDĀ® C3 GF 30 1 black (4363) - PA6.6/6 blend, 30% glass fiber reinforced, heat stabilised, industrial engineering, automotive industry

116171880

AKROMIDĀ®

UL
Preliminary

B3 GF 30 1 HU LA black (2862)PA6 GF30

AKROMIDĀ® B3 GF 30 1 HU LA black (2862) is a 30% glass fibre reinforced, heat ageing resistant polyamide 6 with high rigidity and strength. This UL94 HB listed grade is suitable for technical components in mechanical engineering and the automotive industry. The material is laser markable.

Features

heat stabilised 130
laser markable
E&E
Sports & leisure

Regulatory

ul

Properties

Modulus

10.300MPa

Strength

185MPa

Impact

95kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
10300 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
185 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
3 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
8500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
270 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
30Ā°C | d.a.m.
-
95 kJ/mĀ²
85 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
30Ā°C | d.a.m.
-
13 kJ/mĀ²
12 kJ/mĀ²

UV Exposure and Water Immersion

UL 746C

UL
f2

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
210 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 Ā°C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
150 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 Ā°C

Flammability

Burning rate

UL 94

UL
0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,36 g/cmĀ³

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Electrical Properties

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1012 ā„¦

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more