AKROMIDĀ®

B28 GF 15 2 black (7060)

PA6 GF15

AKROMIDĀ® B28 GF 15 2 black (7060) - 15% glass fibre reinforced, heat- and UV-stabilised, easy flowing polyamide 6, average stiffness and strength, passes ISO 4892-2 with 1200h exposure time.

Modulus

6.100MPa

Strength

108MPa

Impact

32kJ/mĀ²

AKROMIDĀ® B28 GF 15 2 black (7060) - 15% glass fibre reinforced, heat- and UV-stabilised, easy flowing polyamide 6, average stiffness and strength, passes ISO 4892-2 with 1200h exposure time.

AKROMIDĀ®

B3 GF 30 1 black (20000)

PA6 GF30

AKROMIDĀ® B3 GF 30 1 black (20000) - 30% glass fiber reinforced PA 6, heat stabilised for technical parts in industrial engineering, automotive and agricultural machinery industry

Modulus

9.500MPa

Strength

175MPa

Impact

90kJ/mĀ²

AKROMIDĀ® B3 GF 30 1 black (20000) - 30% glass fiber reinforced PA 6, heat stabilised for technical parts in industrial engineering, automotive and agricultural machinery industry

PRECITEĀ®

P3 GF 20 black (7609)

PBT GF20

PRECITEĀ® P3 GF 20 schwarz (7609) - PBT, glass fibre reinforced, higher CTI and very good dimensional stability.

Modulus

7.000MPa

Strength

120MPa

Impact

50kJ/mĀ²

PRECITEĀ® P3 GF 20 schwarz (7609) - PBT, glass fibre reinforced, higher CTI and very good dimensional stability.

PRECITEĀ®

Preliminary

P3 GF 40 black (7591)

PBT GF 40

PRECITEĀ® P3 GF 40 black (7591) is a 40% glass fibre reinforced, medium viscous polybutylene terephthalate (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.

Modulus

13.000MPa

Strength

165MPa

Impact

70kJ/mĀ²

PRECITEĀ® P3 GF 40 black (7591) is a 40% glass fibre reinforced, medium viscous polybutylene terephthalate (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.

AKROMIDĀ®

A3 GF 35 2 black (21010)

PA66 GF35

AKROMIDĀ® A3 GF 35 2 black (21010) is a 35% glass fibre reinforced, UV-stabilised polyamide 6.6 with high stiffness and strength

Modulus

12.000MPa

Strength

185MPa

Impact

50kJ/mĀ²

AKROMIDĀ® A3 GF 35 2 black (21010) is a 35% glass fibre reinforced, UV-stabilised polyamide 6.6 with high stiffness and strength

AKROMIDĀ®

Preliminary

T5 GF 35 6 natural (8005)

PPA GF35

AKROMIDĀ® T5 GF 35 6 natural (8005) is a 35% glass fibre reinforced, inorganic high temperature stabilised polyphthalamide with high rigidity and strength, as well as high temperature and chemical resistance

Modulus

12.500MPa

Strength

230MPa

Impact

70kJ/mĀ²

AKROMIDĀ® T5 GF 35 6 natural (8005) is a 35% glass fibre reinforced, inorganic high temperature stabilised polyphthalamide with high rigidity and strength, as well as high temperature and chemical resistance

AKROMIDĀ®

B3 ICF 15 black (5026)

PA6 CF15

AKROMIDĀ® B3 ICF 15 black (5026) is a 15% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties.

Modulus

11.000MPa

Strength

140MPa

Impact

55kJ/mĀ²

AKROMIDĀ® B3 ICF 15 black (5026) is a 15% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties.

116171880

AKROMIDĀ®

A3 GF 15 1 natural (2308)PA66 GF15

AKROMIDĀ® A3 GF 15 1 natural (2308) is a 15% glass fibre reinforced, polyamide 6.6. It is characterised by average stiffness and strength. Furthermore, the material is heat stabilised and therefore perfectly suitable for technical parts in industrial engineering and in the automotive industry.

Features

heat stabilised 130

Properties

Modulus

6.400MPa

Strength

140MPa

Impact

45kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
6400 MPa
3700 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
140 MPa
80 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,5 %
12 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
6100 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
200 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
45 kJ/mĀ²
90 kJ/mĀ²
43 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
7 kJ/mĀ²
10 kJ/mĀ²
6 kJ/mĀ²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.
200 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
245 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
260 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 Ā°C

Coefficient of linear thermal expansion

ISO 11359-1/2

23Ā°C to 80Ā°C | parallel
23Ā°C to 80Ā°C | transverse
0,34 10ā»ā“/K
1,11 10ā»ā“/K

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
160 - 175 Ā°C
130 - 150 Ā°C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
650 Ā°C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,24 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
2,5 - 2,7 %

Water absorption

ISO 62

23Ā°C, saturated
6,7 - 7,3 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 - 0,5 %
0,9 - 1,1 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
conditioned
1013 ā„¦ x cm
1010 ā„¦ x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
1012 ā„¦
1010 ā„¦

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more