AKROMID®

B28 GF 15 2 black (7060)

PA6 GF15

AKROMID® B28 GF 15 2 black (7060) - 15% glass fibre reinforced, heat- and UV-stabilised, easy flowing polyamide 6, average stiffness and strength, passes ISO 4892-2 with 1200h exposure time.

Modulus

6.100MPa

Strength

108MPa

Impact

32kJ/m²

AKROMID® B28 GF 15 2 black (7060) - 15% glass fibre reinforced, heat- and UV-stabilised, easy flowing polyamide 6, average stiffness and strength, passes ISO 4892-2 with 1200h exposure time.

AKROMID®

B3 GF 30 1 black (20000)

PA6 GF30

AKROMID® B3 GF 30 1 black (20000) - 30% glass fiber reinforced PA 6, heat stabilised for technical parts in industrial engineering, automotive and agricultural machinery industry

Modulus

9.500MPa

Strength

175MPa

Impact

90kJ/m²

AKROMID® B3 GF 30 1 black (20000) - 30% glass fiber reinforced PA 6, heat stabilised for technical parts in industrial engineering, automotive and agricultural machinery industry

PRECITE®

P3 GF 20 black (7609)

PBT GF20

PRECITE® P3 GF 20 schwarz (7609) - PBT, glass fibre reinforced, higher CTI and very good dimensional stability.

Modulus

7.000MPa

Strength

120MPa

Impact

50kJ/m²

PRECITE® P3 GF 20 schwarz (7609) - PBT, glass fibre reinforced, higher CTI and very good dimensional stability.

PRECITE®

Preliminary

P3 GF 40 black (7591)

PBT GF 40

PRECITE® P3 GF 40 black (7591) is a 40% glass fibre reinforced, medium viscous polybutylene terephthalate (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.

Modulus

13.000MPa

Strength

165MPa

Impact

70kJ/m²

PRECITE® P3 GF 40 black (7591) is a 40% glass fibre reinforced, medium viscous polybutylene terephthalate (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.

AKROMID®

A3 GF 35 2 black (21010)

PA66 GF35

AKROMID® A3 GF 35 2 black (21010) is a 35% glass fibre reinforced, UV-stabilised polyamide 6.6 with high stiffness and strength

Modulus

12.000MPa

Strength

185MPa

Impact

50kJ/m²

AKROMID® A3 GF 35 2 black (21010) is a 35% glass fibre reinforced, UV-stabilised polyamide 6.6 with high stiffness and strength

AKROMID®

Preliminary

T5 GF 35 6 natural (8005)

PPA GF35

AKROMID® T5 GF 35 6 natural (8005) is a 35% glass fibre reinforced, inorganic high temperature stabilised polyphthalamide with high rigidity and strength, as well as high temperature and chemical resistance

Modulus

12.500MPa

Strength

230MPa

Impact

70kJ/m²

AKROMID® T5 GF 35 6 natural (8005) is a 35% glass fibre reinforced, inorganic high temperature stabilised polyphthalamide with high rigidity and strength, as well as high temperature and chemical resistance

AKROMID®

B3 ICF 15 black (5026)

PA6 CF15

AKROMID® B3 ICF 15 black (5026) is a 15% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties.

Modulus

11.000MPa

Strength

140MPa

Impact

55kJ/m²

AKROMID® B3 ICF 15 black (5026) is a 15% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties.

116171880

AKROMID®

A3 5 S3 15 black (1434)PA66-I

AKROMID® A3 5 S3 15 black 950058 (1434) is an unreinforced, impact modified Polyamide 6.6. It is characterised by a medium dry impact strength. Furthermore, the material is high heat stabilised and therefore perfectly suitable for connecting and fixing systems which are used at elevated temperatures in the automotive and electro industry.

Features

heat stabilised 160
impact modified

Properties

Modulus

2.500MPa

Strength

65MPa

Impact

180kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
2500 MPa
1200 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
65 MPa
45 MPa

Tensile strain at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
7 %
24 %

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
30 %
> 100 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
95 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
7,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
no break
no break
no break
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
30°C | d.a.m.
-
15 kJ/m²
13 kJ/m²

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,11 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,9 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.