AKROMIDĀ®

B28 GF 30 9 natural (6614)

PA6 GF30

AKROMIDĀ® B28 GF 30 9 natural (6614) - PA 6, 30% glassfiber reinforced, easy flow, good surface, technical parts in industrial engineering and automotive industry

Modulus

10.300MPa

Strength

185MPa

Impact

95kJ/mĀ²

AKROMIDĀ® B28 GF 30 9 natural (6614) - PA 6, 30% glassfiber reinforced, easy flow, good surface, technical parts in industrial engineering and automotive industry

AKROLOYĀ®

PA GF 60 natural (6465)

PA66+PA6I/6T GF60

AKROLOYĀ® PA GF 60 natural (6465) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

Modulus

21.000MPa

Strength

280MPa

Impact

100kJ/mĀ²

AKROLOYĀ® PA GF 60 natural (6465) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

PRECITEĀ®

Preliminary

P3 ICF 40 black (6949)

PBT CF 40

PRECITEĀ® P3 ICF 40 black (6949) - PBT, 40% recycled carbon fibre , very high stiffness and toughness, improved surface finish, good dimensionstability, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.

Modulus

31.000MPa

Strength

190MPa

Impact

50kJ/mĀ²

PRECITEĀ® P3 ICF 40 black (6949) - PBT, 40% recycled carbon fibre , very high stiffness and toughness, improved surface finish, good dimensionstability, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.

PRECITEĀ®

Preliminary

E GF 40 natural (7304)

PET GF 40

PRECITEĀ® E GF 40 natural (7304) - PET, 40 % glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

15.000MPa

Strength

195MPa

Impact

64kJ/mĀ²

PRECITEĀ® E GF 40 natural (7304) - PET, 40 % glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

AKROMIDĀ®

A3 GF 30 4 6 black (13690)

PA66 GF30

AKROMIDĀ® A3 GF 30 4 6 black (13690) - PA6.6, 30% glass fiber, cooling water, hydrolysis resistant, DPPD free

Modulus

10.000MPa

Strength

190MPa

Impact

85kJ/mĀ²

AKROMIDĀ® A3 GF 30 4 6 black (13690) - PA6.6, 30% glass fiber, cooling water, hydrolysis resistant, DPPD free

PRECITEĀ®

Preliminary

P1 GF 30 natural (7062)

PBT GF30

PRECITEĀ® P1 GF 30 natural (7062) is a 30% glass fibre reinforced, low viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

Modulus

9.800MPa

Strength

150MPa

Impact

75kJ/mĀ²

PRECITEĀ® P1 GF 30 natural (7062) is a 30% glass fibre reinforced, low viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

PRECITEĀ®

P3 GF 20 natural (7610)

PBT GF 20

PRECITEĀ® P3 GF 20 natural (7610) is a 20% glass fibre reinforced, lubricated poly butylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

Modulus

7.200MPa

Strength

130MPa

Impact

65kJ/mĀ²

PRECITEĀ® P3 GF 20 natural (7610) is a 20% glass fibre reinforced, lubricated poly butylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

116171880

AKROMIDĀ®

B3 GFM 15/25 black (1312)PA6 (GF15+MD25)

AKROMIDĀ® B3 GFM 15/25 black (1312) is a 15% glass fibre reinforced, 25% mineral filled polyamide 6 with good surface and dimensional stability

Features

surface modified
low warpage

Properties

Modulus

8.000MPa

Strength

120MPa

Impact

50kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
8000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
120 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
3 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
7000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
190 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
50 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
4 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
190 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
216 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
222 Ā°C

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
160 - 175 Ā°C
130 - 150 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,45 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,8 %

Water absorption

ISO 62

23Ā°C, saturated
6,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 %
0,9 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
1012 ā„¦ x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1015 ā„¦

Comparative tracking index

IEC 60112

Test liquid A
400 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.