AKROMID®

B28 GF 50 natural (4842)

PA6 GF50

AKROMID® B28 GF 50 natural (4842) - 50% glass fibre reinforced, easy flowing, polyamide 6, very high stiffness and strength

Modulus

16.500MPa

Strength

250MPa

Impact

110kJ/m²

AKROMID® B28 GF 50 natural (4842) - 50% glass fibre reinforced, easy flowing, polyamide 6, very high stiffness and strength

AKROMID®

C3 GF 35 5 XTC black (5552)

PA66+PA6 GF35

AKROMID® C3 GF 35 5 XTC black (5552) is a 35% glass fibre reinforced, high heat stabilised polyamid 66/6 blend with high stiffness and strength and with extra high temperature tolerance.

Modulus

11.000MPa

Strength

200MPa

Impact

100kJ/m²

AKROMID® C3 GF 35 5 XTC black (5552) is a 35% glass fibre reinforced, high heat stabilised polyamid 66/6 blend with high stiffness and strength and with extra high temperature tolerance.

AKROMID®

T5 GF 40 black (6486)

PPA GF40

AKROMID® T5 GF 40 black (6486) - 40% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

Modulus

14.500MPa

Strength

245MPa

Impact

80kJ/m²

AKROMID® T5 GF 40 black (6486) - 40% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

AKROLOY®

PA FGF 50 black (6546)

PA66+PA6I/6T FGF50

AKROLOY® PA FGF 50 black (6546) - semi-aromatic polyamide blend, 50% flat glass fiber reinforced,improved properties 90° to the flow direction

Modulus

17.000MPa

Strength

265MPa

Impact

100kJ/m²

AKROLOY® PA FGF 50 black (6546) - semi-aromatic polyamide blend, 50% flat glass fiber reinforced,improved properties 90° to the flow direction

AKROMID®

A3 1 S3 black (21002)

PA66-I

AKROMID® A3 1 S3 black (21002) - PA66, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E

Modulus

2.300MPa

Strength

60MPa

Impact

180kJ/m²

AKROMID® A3 1 S3 black (21002) - PA66, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E

AKROTEK®

PK-VM M 10 natural (7575)

PK

AKROTEK® PK-VM M 10 natural (7575) - Polyketon, 10 % mineral reinforced Tribology, friction and wear, chemical resistance, isotropic shrinkage

Modulus

2.900MPa

Strength

58MPa

Impact

50kJ/m²

AKROTEK® PK-VM M 10 natural (7575) - Polyketon, 10 % mineral reinforced Tribology, friction and wear, chemical resistance, isotropic shrinkage

AKROMID®

Preliminary

T5 GF 35 6 natural (8005)

PPA GF35

AKROMID® T5 GF 35 6 natural (8005) is a 35% glass fibre reinforced, inorganic high temperature stabilised polyphthalamide with high rigidity and strength, as well as high temperature and chemical resistance

Modulus

12.500MPa

Strength

230MPa

Impact

70kJ/m²

AKROMID® T5 GF 35 6 natural (8005) is a 35% glass fibre reinforced, inorganic high temperature stabilised polyphthalamide with high rigidity and strength, as well as high temperature and chemical resistance

114151680

AKROMID®

B3 ICF 20 1 L black (5296)PA6 + PP CF20

AKROMID® B3 ICF 20 1 L black (5296) is a 20% carbon fibre reinforced, heat stabilised polyamide-blend with high flexural strength, good sliding properties and a reduced density compared to standard PA6 ICF 20

Features

heat stabilised 130
reduced density

Properties

Modulus

14.200MPa

Strength

140MPa

Impact

50kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
14200 MPa
9700 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
140 MPa
120 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,5 %
4,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
13000 MPa
9700 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
230 MPa
170 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
3 %
5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
50 kJ/m²
60 kJ/m²
45 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
9 kJ/m²
11 kJ/m²
6 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
200 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
222 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

GWIT

IEC 60695-2-13

1,6 mm Wall thickness
675 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,15 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,6 - 1,8 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,4 - 0,6 %

Electrical Properties

Surface resistivity

DIN EN 62631-3-2

d.a.m.
106 Ω

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more