AKROMID®

B3 GF 50 1 black (2488)

PA6 GF50

AKROMID® B3 GF 50 1 black (2488) - 50% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry


Modulus

17.000MPa

Strength

230MPa

Impact

100kJ/m²

AKROMID® B3 GF 50 1 black (2488) - 50% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

B28 LGF 40 1 L black (6155)

PA6 + PP LGF40

AKROMID® B28 LGF 40 1 L black (6155) - PA6/PP-Blend, 40% long glass fiber reinforced, easy flowing, lightweight, low shrinkage, very good fatigue performance


Modulus

12.000MPa

Strength

200MPa

Impact

100kJ/m²

AKROMID® B28 LGF 40 1 L black (6155) - PA6/PP-Blend, 40% long glass fiber reinforced, easy flowing, lightweight, low shrinkage, very good fatigue performance

AKROLOY®

PA FGF 50 black (6546)

PA66+PA6I/6T FGF50

AKROLOY® PA FGF 50 black (6546) - semi-aromatic polyamide blend, 50% flat glass fiber reinforced,improved properties 90° to the flow direction


Modulus

17.000MPa

Strength

265MPa

Impact

100kJ/m²

AKROLOY® PA FGF 50 black (6546) - semi-aromatic polyamide blend, 50% flat glass fiber reinforced,improved properties 90° to the flow direction

PRECITE®

Preliminary

P3 GF 50 black (6925)

PBT GF 50

PRECITE® P3 GF 50 black (6925) is a 50% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.


Modulus

17.000MPa

Strength

175MPa

Impact

60kJ/m²

PRECITE® P3 GF 50 black (6925) is a 50% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.

PRECITE®

P1 natural (7010)

PBT

PRECITE® P1 natural (7010) - PBT, unreinforced, low viscosity, good dimensional stability, automotive, E&E, appliances industries.


Modulus

2.400MPa

Strength

55MPa

Impact

180kJ/m²

PRECITE® P1 natural (7010) - PBT, unreinforced, low viscosity, good dimensional stability, automotive, E&E, appliances industries.

PRECITE®

Preliminary

E GF 40 natural (7304)

PET GF 40

PRECITE® E GF 40 natural (7304) - PET, 40 % glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.


Modulus

15.000MPa

Strength

195MPa

Impact

64kJ/m²

PRECITE® E GF 40 natural (7304) - PET, 40 % glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

AKROMID®

C28 GFM 10/20 5 XTC black (7367)

PA66+PA6 (GF10+MD20)

AKROMID® C28 GFM 10/20 5 XTC black (7367) - 10% glass fiber and 20% mineral reinforced, easy flowing and high heat stabilised, high dimensional stability


Modulus

9.500MPa

Strength

120MPa

Impact

40kJ/m²

AKROMID® C28 GFM 10/20 5 XTC black (7367) - 10% glass fiber and 20% mineral reinforced, easy flowing and high heat stabilised, high dimensional stability

114151680

AKROMID®

B3 GF 40 1 black (20016)PA6 GF40

AKROMID® B3 GF 40 1 black (20016) is a 40% glass fibre reinforced, heat stabilised polyamide 6 with very high stiffness and strength

Features

heat stabilised 130

Properties

Modulus

12.500MPa

Strength

195MPa

Impact

95kJ/m²

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
12500 MPa
8000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
195 MPa
120 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3 %
5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
95 kJ/m²
100 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
15 kJ/m²
21 kJ/m²

Thermal Properties


Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
210 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
165 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability


Burning rate

UL 94

0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties


Density

ISO 1183

23°C
1,46 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,8 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Electrical Properties


Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
conditioned
1013 Ω x cm
1010 Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
1012
1010

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.