AKROMID®
B3 GFM 15/25 black (1312)
PA6 (GF15+MD25)
AKROMID® B3 GFM 15/25 black (1312) is a 15% glass fibre reinforced, 25% mineral filled polyamide 6 with good surface and dimensional stability
8.000MPa
120MPa
50kJ/m²
AKROMID® B3 GFM 15/25 black (1312) is a 15% glass fibre reinforced, 25% mineral filled polyamide 6 with good surface and dimensional stability
AKROMID®
B3 GF 30 S1 natural (1383)
PA6-I GF30
AKROMID® B3 GF 30 S1 natural (1383) - PA 6, 30% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive
7.500MPa
125MPa
110kJ/m²
AKROMID® B3 GF 30 S1 natural (1383) - PA 6, 30% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive
AKROMID®
A3 GF 40 1 black (2386)
PA66 GF40
AKROMID® A3 GF 40 1 black (2386) - 40% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry
13.100MPa
225MPa
100kJ/m²
AKROMID® A3 GF 40 1 black (2386) - 40% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry
AKROMID®
B3 GK 30 black (1827)
PA6 GB30
AKROMID® B3 GK 30 black (1827) - PA 6, 30% glass beads reinforced, good surface, low warpage
4.500MPa
75MPa
20kJ/m²
AKROMID® B3 GK 30 black (1827) - PA 6, 30% glass beads reinforced, good surface, low warpage
AKROMID®
A3 GF 30 1 black (2385)
PA66 GF30
AKROMID® A3 GF 30 1 black (2385) - PA 6.6 30% glass fiber reinforced, heat stabilised, technical parts in industrial engineering and in the automotive industry
10.000MPa
200MPa
85kJ/m²
AKROMID® A3 GF 30 1 black (2385) - PA 6.6 30% glass fiber reinforced, heat stabilised, technical parts in industrial engineering and in the automotive industry
AKROMID®
A3 GF 30 1 natural (2391)
PA66 GF30
AKROMID® A3 GF 30 1 natural (2391) - PA 6.6 30% glass fiber reinforced, heat stabilised, technical parts in industrial engineering and in the automotive industry
10.000MPa
200MPa
85kJ/m²
AKROMID® A3 GF 30 1 natural (2391) - PA 6.6 30% glass fiber reinforced, heat stabilised, technical parts in industrial engineering and in the automotive industry
AKROMID®
B3 GF 30 natural (2472)
PA6 GF30
AKROMID® B3 GF 30 natural (2472) - 30% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry
10.300MPa
185MPa
95kJ/m²
AKROMID® B3 GF 30 natural (2472) - 30% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry
AKROLOY®
PARA GF 50 HU black (8596)PARA GF50
AKROLOY® PARA GF 50 HU black (8596) is a 50% glass fibre reinforced polyarylamid with very high stiffness and strength, even in conditioned state.Even in conditioned state, it impresses with very high stiffness and strength owing to its lower moisture uptake. Furthermore, the material shows very good flowability and surface properties. It is perfectly suitable for parts where dimensional stabilitiy is required. Besides, it can be used as an alternative for aluminium and zinc diecast alloys. The material is listed at UL in all colors.
Features
Regulatory
Properties
19.700MPa
295MPa
78kJ/m²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Temperature of deflection under load HDT/C
ISO 75
Glass transition temperature
ISO 11357-2
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
HWI
UL 746A
HAI
UL 746A
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Water absorption
ISO 62
Molding shrinkage
ISO 294-4
Electrical Properties
Comparative tracking index
IEC 60112
Comparative tracking index
ASTM D3638
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.