AKROMID®

NEXT B3 GF 40 black (6077BMBCI)PA6 GF40

AKROMID® NEXT B3 GF 40 black (6077BMBCI) is a 40% glass fiber reinforced, heat stabilised polyamide 6. It is characterised by a very high stiffness and strength. The material is perfectly suitable for safety-related parts in the automotive interior. The material is certified according to ISCC PLUS. 57% ISCC-certified bio-circular material is sourced and attributed to the compound following the ISCC mass balance approach.

Features

mass balanced

Properties

Modulus

Na

Strength

Na

Impact

110kJ/m²

Sustainability Aspects

Percentage of certified material

only valid for ISCC PLUS certified products

57 %

Mechanical Properties

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
40°C | d.a.m.
-
110 kJ/m²
106 kJ/m²
105 kJ/m²
100 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
40°C | d.a.m.
-
20 kJ/m²
30 kJ/m²
15 kJ/m²
15 kJ/m²

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Similar products

AKRO Compound Explorer

AKROMID®

NEXT B3 GF 50 1 black (2488BMBCI)

PA6 GF50

AKROMID® NEXT B3 GF 50 1 black (2488BMBCI) is a 50 % glass fiber reinforced polyamide 6. It is characterised by a very high stiffness and strength. Furthermore, the material is heat stabilised and therefore perfectly suitable for technical parts in i

Modulus

17.000MPa

Strength

230MPa

Impact

100kJ/m²

AKROMID®

B3 GF 50 S1 black (2000)

PA6-I GF50

AKROMID® B3 GF 50 S1 black 950089 (2000) is a 50% glass fiber reinforced, impact modified Polyamide 6. It is characterised by very high stiffness and strength as well as a higher notched impact strength compared to a standard PA 6 GF 50. The material

Modulus

15.000MPa

Strength

190MPa

Impact

100kJ/m²

AKROMID®

B3 GF 40 1 black (2487)

PA6 GF40

AKROMID® B3 GF 40 1 black (2487) is a 40% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength.

Modulus

12.800MPa

Strength

205MPa

Impact

100kJ/m²

AKROMID®

B3 GF 50 1 black (2488)

PA6 GF50

AKROMID® B3 GF 50 1 black (2488) is a 50% glass fiber reinforced polyamide 6. It is characterised by a very high stiffness and strength. Furthermore, the material is heat stabilised and therefore perfectly suitable for technical parts in industrial e

Modulus

17.000MPa

Strength

215MPa

Impact

90kJ/m²

AKROMID®

B3 GF 50 RM-M black (3146)

PA6+X GF50

AKROMID® B3 GF 50 RM-M black (3146) is a 50% glass fiber reinforced polyamide 6. The material is characterised by very high stiffness and strength as well as reduced moisture absorption. As a result, there will be less changes of the mechanical prope

Modulus

17.000MPa

Strength

210MPa

Impact

70kJ/m²

AKROMID®

B3 GF 50 2 S1 black (3050)

PA6-I GF50

AKROMID® B3 GF 50 2 S1 black (3050) is a 50% glass fiber reinforced, impact modified Polyamide 6. It is characterised by very high stiffness and strength as well as a higher notched impact strength compared to a standard PA 6 GF 50. Furthermore, it i

Modulus

15.000MPa

Strength

195MPa

Impact

110kJ/m²

AKROMID®

B3 GF 45 1 black (3851)

PA6 GF45

AKROMID® B3 GF 45 1 black (3851) is a 45% glass fibre reinforced, heat stabilised polyamide 6 with very high rigidity and strength

Modulus

14.500MPa

Strength

200MPa

Impact

110kJ/m²

AKROMID®

B28 GF 50 1 GIT black (4732)

PA6 GF50

AKROMID® B28 GF 50 1 GIT black (4732) is a 50% glass fibre reinforced, heat stabilised, easy flowing polyamide 6 with very high stiffness and strength for gas injection technology.

Modulus

16.700MPa

Strength

235MPa

Impact

105kJ/m²

AKROMID®

B3 GF 50 black (4907)

PA6 GF50

AKROMID® B3 GF 50 black (4907) is a 50% glass fibre reinforced high-flow polyamide 6 with very high rigidity and strength. The material is suitable for technical components in mechanical engineering, automotive industry as well as construction indu

Modulus

17.000MPa

Strength

240MPa

Impact

100kJ/m²

AKROMID®

B3 GF 45 1 black (5744)

PA6 GF45

AKROMID® B3 GF 45 1 black (5744) is a 45% glass fibre reinforced, heat stabilised polyamide 6 with very high rigidity and strength as well as improved impact

Modulus

14.000MPa

Strength

200MPa

Impact

110kJ/m²

AKROMID®

B3 GF 40 black (6077)

PA6 GF40

AKROMID® B3 GF 40 black (6077) is a 40% glass fiber reinforced, heat stabilised polyamide 6. It is characterised by a very high stiffness and strength. The material is perfectly suitable for safety-related parts in the automotive interior.

Modulus

12.500MPa

Strength

200MPa

Impact

105kJ/m²

AKROMID®

B3 GF 40 5 black (7286)

PA6 GF40

AKROMID® B3 GF 40 5 black (7286) is a 40% glass fiber reinforced polyamide 6. It is characterised by a very high stiffness and strength. Furthermore, the material is high heat stabilised and therefore perfectly suitable for technical parts which are

Modulus

12.500MPa

Strength

200MPa

Impact

95kJ/m²