AKROMID®

B3 GF 40 black (6077)PA6 GF40

AKROMID® B3 GF 40 black (6077) is a 40% glass fiber reinforced, heat stabilised polyamide 6. It is characterised by a very high stiffness and strength. The material is perfectly suitable for safety-related parts in the automotive interior.

Properties

Modulus

12.500MPa

Strength

200MPa

Impact

105kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
12500 MPa
8000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
200 MPa
135 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,8 %
7 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
12500 MPa
7600 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
320 MPa
210 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
40°C | d.a.m.
-
105 kJ/m²
110 kJ/m²
95 kJ/m²
90 kJ/m²
100 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
40°C | d.a.m.
-
17 kJ/m²
25 kJ/m²
14 kJ/m²
15 kJ/m²
15 kJ/m²

Ball indentation hardness

ISO 2039-1

358N/30s | conditioned
961N/30s | d.a.m.
105 MPa
213 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
215 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
170 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Coefficient of linear thermal expansion

ISO 11359-1/2

23°C to 80°C | parallel
23°C to 80°C | transverse
0,14 10⁻⁴/K
1,07 10⁻⁴/K

Vicat softening temperature B50

ISO 306

50°C/50N
215 °C

Flammability

Flammability

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General Properties

Density

ISO 1183

23°C
1,46 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,5 - 1,8 %

Water absorption

ISO 62

23°C, saturated
5,4 - 5,6 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Electrical Properties

Volume resistivity

IEC 62631-3-1

d.a.m.
conditioned
1013 Ω x cm
1010 Ω x cm

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Similar products

AKRO Compound Explorer

AKROMID®

B3 GF 50 S1 black (2000)

PA6-I GF50

AKROMID® B3 GF 50 S1 black 950089 (2000) is a 50% glass fiber reinforced, impact modified Polyamide 6. It is characterised by very high stiffness and strength as well as a higher notched impact strength compared to a standard PA 6 GF 50. The material

Modulus

15.000MPa

Strength

190MPa

Impact

100kJ/m²

AKROMID®

B3 GF 40 1 black (2487)

PA6 GF40

AKROMID® B3 GF 40 1 black (2487) is a 40% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength.

Modulus

12.800MPa

Strength

205MPa

Impact

100kJ/m²

AKROMID®

B3 GF 50 1 black (2488)

PA6 GF50

AKROMID® B3 GF 50 1 black (2488) is a 50% glass fiber reinforced polyamide 6. It is characterised by a very high stiffness and strength. Furthermore, the material is heat stabilised and therefore perfectly suitable for technical parts in industrial e

Modulus

17.000MPa

Strength

220MPa

Impact

100kJ/m²

AKROMID®

B3 GF 35 1 black (2486)

PA6 GF35

AKROMID® B3 GF 35 1 black (2486) is a 35% glass fibre reinforced, heat stabilised Polyamid 6 with high stiffness and strength.

Modulus

11.500MPa

Strength

195MPa

Impact

100kJ/m²

AKROMID®

B3 GF 50 RM-M black (3146)

PA6+X GF50

AKROMID® B3 GF 50 RM-M black (3146) is a 50% glass fiber reinforced polyamide 6. The material is characterised by very high stiffness and strength as well as reduced moisture absorption. As a result, there will be less changes of the mechanical prope

Modulus

17.000MPa

Strength

210MPa

Impact

70kJ/m²

AKROMID®

B3 GF 50 2 S1 black (3050)

PA6-I GF50

AKROMID® B3 GF 50 2 S1 black (3050) is a 50% glass fiber reinforced, impact modified Polyamide 6. It is characterised by very high stiffness and strength as well as a higher notched impact strength compared to a standard PA 6 GF 50. Furthermore, it i

Modulus

15.000MPa

Strength

195MPa

Impact

110kJ/m²

AKROMID®

B3 GF 45 1 black (3851)

PA6 GF45

AKROMID® B3 GF 45 1 black (3851) is a 45% glass fibre reinforced, heat stabilised polyamide 6 with very high rigidity and strength

Modulus

14.500MPa

Strength

200MPa

Impact

110kJ/m²

AKROMID®

B28 GF 50 1 GIT black (4732)

PA6 GF50

AKROMID® B28 GF 50 1 GIT black (4732) is a 50% glass fibre reinforced, heat stabilised, easy flowing polyamide 6 with very high stiffness and strength for gas injection technology.

Modulus

16.700MPa

Strength

235MPa

Impact

105kJ/m²

AKROMID®

B3 GF 50 black (4907)

PA6 GF50

AKROMID® B3 GF 50 black (4907) is a 50% glass fibre reinforced high-flow polyamide 6 with very high rigidity and strength. The material is suitable for technical components in mechanical engineering, automotive industry as well as construction indu

Modulus

17.000MPa

Strength

240MPa

Impact

100kJ/m²

AKROMID®

B3 GF 45 1 black (5744)

PA6 GF45

AKROMID® B3 GF 45 1 black (5744) is a 45% glass fibre reinforced, heat stabilised polyamide 6 with very high rigidity and strength as well as improved impact

Modulus

14.000MPa

Strength

200MPa

Impact

110kJ/m²

AKROMID®

B3 GF 40 5 black (7286)

PA6 GF40

AKROMID® B3 GF 40 5 black (7286) is a 40% glass fiber reinforced polyamide 6. It is characterised by a very high stiffness and strength. Furthermore, the material is high heat stabilised and therefore perfectly suitable for technical parts which are

Modulus

12.500MPa

Strength

200MPa

Impact

95kJ/m²

AKROMID®

B3 GF 50 1 black (20008)

PA6 GF50

AKROMID® B3 GF 50 black (20008) is a 50% glass fiber reinforced polyamide 6. It is characterised by a very high stiffness and strength. Furthermore, the material is heat stabilised and therefore perfectly suitable for technical parts in industrial en

Modulus

17.000MPa

Strength

210MPa

Impact

80kJ/m²