NEXT 5.6 3 GF 30 natural (8405)PA5.6 GF30

AKROMID® NEXT 5.6 3 GF 30 natur (8405) is a HMD-free (hexamethylenediamine) alternative to PA 6.6. The partly bio-based material with 30% glass fibre is suitable for parts with high demands on stiffness and strength.

Features

Bio-based
heat stabilised 130
Sports & leisure

Properties

Modulus

9.500MPa

Strength

185MPa

Impact

66kJ/m²

Sustainability

Biobased carbon content

40 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
9500 MPa
5900 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
185 MPa
121 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,8 %
5,1 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
66 kJ/m²
75 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
10 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
236 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
254 °C

Flammability

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General Properties

Density

ISO 1183

23°C
1,36 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,2 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.