AKROMID®

Preliminary

C3 GF 30 8 natural (8103)PA66+PA6 GF30

AKROMID® C3 GF 30 8 natural (8103) is 30% glass fiber reinforced PA6.6/6 Blend with average rigidity and strength. The material corresponds to the European food guideline EU 10/2011 and to the American FDA 21 CFR. This grade is suitable for parts of kitchen and household appliances.

Properties

Modulus

10.000MPa

Strength

185MPa

Impact

75kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
10000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
185 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
4 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
75 kJ/m²

Flammability

Flammability

UL 94

1,6 mm Wall thickness
HB Class

General Properties

Density

ISO 1183

23°C
1,36 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,6 - 0,8 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Similar products

AKRO Compound Explorer

AKROMID®

C3 GF 30 5 XTC natural (4499)

PA66+PA6 GF30

AKROMID® C3 GF 30 5 XTC natural (4499) is a 30% glass fibre reinforced, high temperature stabilised polaymide 6.6/6 - Blend with high stiffness and strength and extra high temperature tolerance.

Modulus

9.500MPa

Strength

185MPa

Impact

95kJ/m²

AKROMID®

UL

C3 GF 25 1 FR natural (7208)

PA66+PA6 GF25 FR(44)

AKROMID® C3 GF 25 1 FR natural (7208) is a 25 % glass fiber reinforced, flame retardant and heat stabilised PA6/6.6 blend.This material is listed in all colors according to UL 94 including excellent RTI values. It is based on a halogen- and antimony

Modulus

9.200MPa

Strength

140MPa

Impact

73kJ/m²

AKROMID®

UL

C3 GF 30 1 FR natural (7207)

PA66+PA6 GF30 FR(44)

AKROMID® C3 GF 30 1 FR natural (7207) is a 30 % glass fiber reinforced, flame retardant and heat stabilised PA6/6.6. This material is listed in all colors according to UL 94 including excellent RTI values. It is based on a halogen- and antimony trio

Modulus

10.700MPa

Strength

150MPa

Impact

76kJ/m²

AKROMID®

Preliminary

C3 GF 30 1 natural (8574)

PA66 + PA6 GF30

AKROMID® C3 GF 30 1 natural (8574) is a 30% glass fiber reinforced, heat stabilised polyamide 6.6/6 blend. It is characterised by high stiffness and strength as well as by higher temperature resistance compared to standard PA6.6/6-blends. It is there

Modulus

9.300MPa

Strength

185MPa

Impact

75kJ/m²

AKROMID®

UL

NEXT C3 GF 30 1 FR natural (7207BMBCI)

PA66+PA6 GF30 FR(44)

AKROMID® NEXT C3 GF 30 1 FR natural (7207BMBCI) is a 30 % glass fiber reinforced, flame retardant and heat stabilised PA6/6.6 blend. It is based on a halogen- and antimony trioxide-free flame retardant system that is also free of red phosphorus, zinc

Modulus

10.700MPa

Strength

150MPa

Impact

76kJ/m²

AKROMID®

UL

NEXT C3 GF 25 1 FR natural (7208BMBCI)

PA66+PA6 GF25 FR(44)

AKROMID® NEXT C3 GF 25 1 FR natural (7208BMBCI) is a 25 % glass fiber reinforced, flame retardant and heat stabilised PA6/6.6 blend. It is based on a halogen- and antimony trioxide-free flame retardant system that is also free of red phosphorus, zinc

Modulus

9.200MPa

Strength

140MPa

Impact

73kJ/m²

AKROMID®

C28 GF 25 FRT natural (7332)

PA-Blend GF25 FR(44)

C28 GF 25 FRT natural (7332) is a 25 % glass fiber reinforced, flame retardant and easy flowing PA blend. The material is based on a flame retardant system that is free of red phosphorus and halogens. This grade is suitable for railroad applications

Modulus

10.800MPa

Strength

157MPa

Impact

64kJ/m²

AKROMID®

B3 GF 30 S1 natural (1383)

PA6-I GF30

AKROMID® B3 GF 30 S1 natural (1383) is a 30% glass fiber reinforced, impact modified Polyamide 6. It is characterised by high stiffness and strength as well as a higher impact strength compared to a standard PA 6 GF 30. The material is therefore perf

Modulus

8.000MPa

Strength

125MPa

Impact

110kJ/m²

AKROMID®

A3 GF 25 1 natural (2390)

PA66 GF25

AKROMID® A3 GF 25 1 natural (2390) is a 25% glass fibre reinforced, heat stabilised polyamide 6.6 with high stiffness and strength and light inherent color.

Modulus

8.500MPa

Strength

185MPa

Impact

70kJ/m²

AKROMID®

A3 GF 30 1 natural (2391)

PA66 GF30

AKROMID® A3 GF 30 1 natural (2391) is a 30% glass fiber reinforced polyamide 6.6. It is characterised by high stiffness and strength. Furthermore, the material is heat stabilised and therefore perfectly suitable for technical parts in industrial engi

Modulus

10.000MPa

Strength

195MPa

Impact

70kJ/m²

AKROMID®

B3 GF 30 natural (2472)

PA6 GF30

AKROMID® B3 GF 30 natural (2472) is a 30% glass fiber reinforced polyamide 6. It is characterised by a high stiffness and strength. The material is therefore perfectly suitable for technical parts in industrial engineering and in the automotive indus

Modulus

10.300MPa

Strength

185MPa

Impact

95kJ/m²

AKROMID®

B3 GF 25 1 natural (2463)

PA6 GF25

AKROMID® B3 GF 25 1 natural (2463) is a 25% glass fibre reinforced, heat stabilised polyamide 6 with high stiffness and strength and light inherent color

Modulus

8.500MPa

Strength

160MPa

Impact

85kJ/m²