AKROMID®

Preliminary

B3 GF 40 natural (8956)PA6 GF40

AKROMID® B3 GF 40 natural (8956) is a 40% glass fiber reinforced Polyamide 6 compound. It is characterized by high stiffness and strength, making it well suited for applications in industrial engineering and automotive components. For adhesive coating or rubber vulcanization, no additional surface pretreatment is required.

Features

surface modified
adhesion modified
process improved

Properties

Modulus

13.000MPa

Strength

200MPa

Impact

100kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
13000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
200 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
3,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
100 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
215 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
170 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Flammability

UL 94

0,8 mm Wall thickness
HB Class

General Properties

Density

ISO 1183

23°C
1,46 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,5 - 1,8 %

Water absorption

ISO 62

23°C, saturated
5,4 - 5,6 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Similar products

AKRO Compound Explorer

AKROMID®

B28 GF 30 9 natural (6614)

PA6 GF30

AKROMID® B28 GF 30 9 natural (6614) is a 30% glass fibre reinforced, easy flowing polyamide 6. The material is characterised by good surface properties due to its very good flowability. Furthermore, the material is easy to color. Owing to its high st

Modulus

10.300MPa

Strength

185MPa

Impact

95kJ/m²

AKROMID®

Preliminary

B3 GKM 40 natural (8630)

PA6 (GB+MD)40

AKROMID® B3 GKM 40 natur (8630) is a 40 % mineral and glass beads filled polyamide 6. The material is characterised by its excellent surface properties and low warpage. It is suitable for use in housings, switches and covers of all kinds in the sanit

Modulus

4.900MPa

Strength

70MPa

Impact

150kJ/m²

AKROMID®

B3 GF 30 AM natural (8962)

PA6 GF30

AKROMID® B3 GF 30 AM natural (8962) is a 30% glass fiber reinforced polyamide 6 with high stiffness and good sliding properties as well as optimized viscosity. It is suitable for pellet-based large format additive manufacturing processes (LFAM, FGF)

Modulus

8.500MPa

Strength

145MPa

Impact

80kJ/m²

AKROMID®

C28 GF 25 FRT natural (7332)

PA-Blend GF25 FR(44)

C28 GF 25 FRT natural (7332) is a 25 % glass fiber reinforced, flame retardant and easy flowing PA blend. The material is based on a flame retardant system that is free of red phosphorus and halogens. This grade is suitable for railroad applications

Modulus

10.800MPa

Strength

157MPa

Impact

64kJ/m²

AKROMID®

B3 GF 35 natural (2473)

PA6 GF35

AKROMID® B3 GF 35 natural (2473) is a 35% glass fiber reinforced polyamide 6. It is characterised by a high stiffness and strength and is therefore perfectly suitable for technical parts in industrial engineering and in the automotive industry. The m

Modulus

11.500MPa

Strength

195MPa

Impact

100kJ/m²

AKROMID®

B3 GF 40 1 natural (2466)

PA6 GF40

AKROMID® B3 GF 40 1 natural (2466) is a 40% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength and light inherent color

Modulus

12.800MPa

Strength

205MPa

Impact

100kJ/m²

AKROMID®

B3 GF 50 1 natural (2531)

PA6 GF50

AKROMID® B3 GF 50 1 natural (2531) is a 50% glass fiber reinforced polyamide 6. It is characterised by a very high stiffness and strength. Furthermore, the material is heat stabilised and therefore perfectly suitable for technical parts in industrial

Modulus

17.000MPa

Strength

230MPa

Impact

100kJ/m²

AKROMID®

B3 GF 50 S1 natural (3694)

PA6-I GF50

AKROMID® B3 GF 50 S1 natural (3694) is a 50% glass fiber reinforced, impact modified Polyamide 6. It is characterised by very high stiffness and strength as well as a higher notched impact strength compared to a standard PA 6 GF 50. The material is t

Modulus

14.500MPa

Strength

190MPa

Impact

110kJ/m²

AKROMID®

B3 GF 50 8 natural (4301)

PA6 GF50

AKROMID® B3 GF 50 8 natural (4301) is a 50% glass fibre reinforced polyamide 6 with very high rigidity and strength. The material corresponds to the European food guideline EU 10/2011 and to the American FDA 21 CFR. This grade is suitable for parts

Modulus

17.000MPa

Strength

240MPa

Impact

100kJ/m²

AKROMID®

B28 GF 60 9 black (4662)

PA6 GF60

AKROMID® B28 GF 60 9 black (4662) is a 60% glass fibre reinforced, process improved, easy flowing polyamide 6 with very high stiffness and strength as well as improved surface quality. Colored without carbon black.

Modulus

21.000MPa

Strength

250MPa

Impact

90kJ/m²

AKROMID®

B28 GF 50 1 GIT black (4732)

PA6 GF50

AKROMID® B28 GF 50 1 GIT black (4732) is a 50% glass fibre reinforced, heat stabilised, easy flowing polyamide 6 with very high stiffness and strength for gas injection technology.

Modulus

16.700MPa

Strength

235MPa

Impact

105kJ/m²

AKROMID®

B28 GF 50 natural (4842)

PA6 GF50

AKROMID® B28 GF 50 natural (4842) - is a 50% glass fiber reinforced polyamide 6. It is characterised by an improved flowability compared to a standard PA 6 GF 50. Furthermore, the material impresses with its high stiffness and strength. It is therefo

Modulus

16.500MPa

Strength

250MPa

Impact

110kJ/m²