AKROMID®

Preliminary

NEXT 5.10 3 GF 30 black (8467)

PA5.10 GF30

AKROMID® NEXT 5.10 3 GF 30 black (8467) - PA 5.10, 100% biobased, HMD-free, glass fibre reinforced, heat stabilised, high strength, E&E, automotive, sports and leisure, construction industry.

Modulus

8.300MPa

Strength

160MPa

Impact

72kJ/m²

AKROMID® NEXT 5.10 3 GF 30 black (8467) - PA 5.10, 100% biobased, HMD-free, glass fibre reinforced, heat stabilised, high strength, E&E, automotive, sports and leisure, construction industry.

AKROMID®

B28 GF 30 S3 white (8349)

PA6-I GF30

AKROMID® B28 GF 30 S3 white (8349) - PA6, 30% glass fibre reinforced, easy flowing and impact modified, for applications in the furniture industry

Modulus

8.900MPa

Strength

150MPa

Impact

94kJ/m²

AKROMID® B28 GF 30 S3 white (8349) - PA6, 30% glass fibre reinforced, easy flowing and impact modified, for applications in the furniture industry

PRECITE®

Preliminary

K GF 15 ECO black (8328)

PBT-PET- GF 15

PRECITE® K GF 15 ECO black (8328) - PBT/PET blend, recycled PET content, 30% glass fiber, good strength, good surface, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.

Modulus

5.900MPa

Strength

105MPa

Impact

35kJ/m²

PRECITE® K GF 15 ECO black (8328) - PBT/PET blend, recycled PET content, 30% glass fiber, good strength, good surface, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.

AKROMID®

Preliminary

B28 GM 10/20 6 black (8640)

PA6 (GF10+GB20)

B28 GM 10/20 6 black (8640) - PA 6 with 10% glass fibers and 20% glass beads reinforced, easy flowing with good surface properties.

Modulus

5.500MPa

Strength

100MPa

Impact

50kJ/m²

B28 GM 10/20 6 black (8640) - PA 6 with 10% glass fibers and 20% glass beads reinforced, easy flowing with good surface properties.

AKROMID®

NEXT S3 GF 30 S1 black (8887)

PA610-I GF30

AKROMID® NEXT S3 GF 30 S1 black (8887) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, impact modified, household, industrial application.

Modulus

7.800MPa

Strength

135MPa

Impact

100kJ/m²

AKROMID® NEXT S3 GF 30 S1 black (8887) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, impact modified, household, industrial application.

PRECITE®

Preliminary

P3 GF 20 8 natural (8456)

PBT GF20

PRECITE® P3 GF 20 natural (8456) - PBT, 20% glass fibre, food contact, very good dimensional stability, kitchen and household appliances.

Modulus

7.200MPa

Strength

125MPa

Impact

65kJ/m²

PRECITE® P3 GF 20 natural (8456) - PBT, 20% glass fibre, food contact, very good dimensional stability, kitchen and household appliances.

PRECITE®

Preliminary

K GF 50 8 black (8446)

PBT+PET GF50

PRECITE® K GF 50 8 black (8446) - PBT/PET blend, 50% glass fibre, very high strength, low moisture absorption, very good dimensional stability, food contact, very good surface, kitchen and household appliances.

Modulus

17.500MPa

Strength

175MPa

Impact

60kJ/m²

PRECITE® K GF 50 8 black (8446) - PBT/PET blend, 50% glass fibre, very high strength, low moisture absorption, very good dimensional stability, food contact, very good surface, kitchen and household appliances.

129303180

PRECITE®

Preliminary

P3 GF 40 natural (6943)PBT GF 40

PRECITE® P3 GF 40 natural (6943) is a 40% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.

Properties

Modulus

13.500MPa

Strength

175MPa

Impact

70kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
13500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
175 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
2,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
12500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
270 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
70 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
13 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
215 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
225 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
725 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,59 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,2 %

Water absorption

ISO 62

23°C, saturated
0,4 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,6 - 0,8 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
> 1013 Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1012 Ω

Comparative tracking index

IEC 60112

Test liquid A
400 V

Rheological Properties

MVR

ISO 1133

250°C/2,16kg
5 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.