NEXT 5.10 3 GF 30 black (8467)

PA5.10 GF30

AKROMID® NEXT 5.10 3 GF 30 black (8467) is a glass fibre reinforced and heat stabilised PA 5.10. The 100 % biobased PA 5.10 is a HMD-free (hexamethylenediamine) alternative to PA 6.10. With 30% glass fibre reinforcement, the material is suitable for components with high strength requirements for E&E, automotive, sports and leisure and construction industry.

Features

Bio-based
heat stabilised 130
electrically neutral
E&E
Sports & leisure

Properties

Modulus

8.300MPa

Strength

160MPa

Impact

72kJ/m²

Sustainability


Biobased carbon content

96 %

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
8300 MPa
6000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
160 MPa
120 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,2 %
4,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
72 kJ/m²
74 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
13 kJ/m²
14 kJ/m²

Thermal Properties


Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
194 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
217 °C

General properties


Density

ISO 1183

23°C
1,29 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,2 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.