AKROMID®

Preliminary

B3 GF 40 1 black (8353)

PA6 GF40

AKROMID® B3 GF 40 1 black (8353) - PA 6, 40% glass fiber reinforced with excellent bonding to LSR, low emission and heat stabilised

Modulus

13.000MPa

Strength

195MPa

Impact

100kJ/m²

AKROMID® B3 GF 40 1 black (8353) - PA 6, 40% glass fiber reinforced with excellent bonding to LSR, low emission and heat stabilised

AKROMID®

C28 GF 25 FRT grey (8133)

PA-Blend

AKROMID® C28 GF 25 FRT grey (8133) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 7011, Public Transportation EN 45545-2.

Modulus

11.000MPa

Strength

150MPa

Impact

NA

AKROMID® C28 GF 25 FRT grey (8133) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 7011, Public Transportation EN 45545-2.

AKROLOY®

PA FGF 50 black (6546)

PA66+PA6I/6T FGF50

AKROLOY® PA FGF 50 black (6546) - semi-aromatic polyamide blend, 50% flat glass fiber reinforced,improved properties 90° to the flow direction

Modulus

17.000MPa

Strength

265MPa

Impact

100kJ/m²

AKROLOY® PA FGF 50 black (6546) - semi-aromatic polyamide blend, 50% flat glass fiber reinforced,improved properties 90° to the flow direction

PRECITE®

Preliminary

P3 natural (7009)

PBT

PRECITE® P3 natural (7009) - PBT, unreinforced, medium viscosity, good dimensional stability, automotive, E&E, appliances industries.

Modulus

2.400MPa

Strength

55MPa

Impact

180kJ/m²

PRECITE® P3 natural (7009) - PBT, unreinforced, medium viscosity, good dimensional stability, automotive, E&E, appliances industries.

AKROMID®

UL

A3 GF 30 FR orange (7871)

PA66 GF30 FR(40)

AKROMID® A3 GF 30 FR orange (7871) is a 30% glass fibre reinforced, halogen free flame retardant polyamide 6.6 listed at UL in all colors. This material is coloured similar RAL2003

Modulus

10.400MPa

Strength

140MPa

Impact

60kJ/m²

AKROMID® A3 GF 30 FR orange (7871) is a 30% glass fibre reinforced, halogen free flame retardant polyamide 6.6 listed at UL in all colors. This material is coloured similar RAL2003

PRECITE®

Preliminary

P3 GF 30 9 FR natural (8053)

PBT GF30 FR(40)

PRECITE® P3 GF 30 9 FR natural (8053) - PBT, 30% glass fiber, flame retardant, high stiffness and strength, good long-term heat-aging, E-Mobility, E&E industry.

Modulus

10.500MPa

Strength

122MPa

Impact

50kJ/m²

PRECITE® P3 GF 30 9 FR natural (8053) - PBT, 30% glass fiber, flame retardant, high stiffness and strength, good long-term heat-aging, E-Mobility, E&E industry.

AKROMID®

D3 GF 30 1 LT black (5391)

PA612 GF30

AKROMID® D3 GF 30 1 LT black (5391) - PA 6.12, glass fiber, laser-transparent,connector

Modulus

9.200MPa

Strength

170MPa

Impact

85kJ/m²

AKROMID® D3 GF 30 1 LT black (5391) - PA 6.12, glass fiber, laser-transparent,connector

120212280

AKROLOY®

UL

PARA GF 50 HU black (8596)PARA GF50

AKROLOY® PARA GF 50 HU black (8596) is a 50% glass fibre reinforced polyarylamid with very high stiffness and strength, even in conditioned state.Even in conditioned state, it impresses with very high stiffness and strength owing to its lower moisture uptake. Furthermore, the material shows very good flowability and surface properties. It is perfectly suitable for parts where dimensional stabilitiy is required. Besides, it can be used as an alternative for aluminium and zinc diecast alloys. The material is listed at UL in all colors.

Features

reduced moisture
easy flow
metal substitution

Regulatory

ul

Properties

Modulus

19.700MPa

Strength

295MPa

Impact

78kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
19700 MPa
19700 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
295 MPa
270 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,0 %
2,0 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
78 kJ/m²
90 kJ/m²
60 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
15 kJ/m²
14 kJ/m²
17 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
230 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
200 °C

Glass transition temperature

ISO 11357-2

DSC, 2nd heating
87 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
238 °C

Flammability

Burning rate

UL 94

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
HB Class
HB Class
HB Class

HWI

UL 746A

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
4 PLC
2 PLC
2 PLC

HAI

UL 746A

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
0 PLC
0 PLC
0 PLC

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,65 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,8 %

Water absorption

ISO 62

23°C, saturated
3,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,2 %
0,2 - 0,4 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
> 600 V

Comparative tracking index

ASTM D3638

UL
0 PLC

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.