AKROMID®
T9 CGM 15/20 LA black (8888)PPA (CF15+GF20)
AKROMID® T9 CGM 15/20 1 LA black (8888) is a 15% carbon fiber and 20% glass fiber reinforced polyphthalamide with high stiffness and strength, as well as high chemical resistance. The compound impresses with its electrical conductivity and is therefore ideal for applications in the automotive sector and industry. The product is based on PA9T and therefore has significantly lower moisture absorption compared to conventional PA6T types. As a result, the glass transition region is significantly more constant and strength remains at a higher level even at higher temperatures, even in the conditioned state.
Features
Properties
15.800MPa
215MPa
65kJ/m²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Charpy impact strength
ISO 179-1/1eU
Thermal Properties
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
General Properties
Density
ISO 1183
Electrical Properties
Surface resistivity
IEC 62631-3-2
Documents
Discover all the technical specifications at a single glance here.
Processing information
The values mentioned are recommendations. We only recommend desiccant / dry air dryers or vacuum dryers. Too long a drying time and the resulting residual moisture content below the lower limit can lead to filling problems and surface defects. The specified drying time refers to closed and undamaged bagged material. When processing from previously opened bags or from octabins with polyolefin inliners, a longer drying time may be necessary. It is recommended to check the residual moisture content after the drying process.
Drying time
0 - 4 h
Drying temperature (τ ≤ -30°C)
120 °C
Processing moisture
<0,05 %
Feed section
60 - 90 °C
Temperature Zone 1 - Zone 4
300 - 340 °C
Nozzle temperature
310 - 350 °C
Melt temperature
310 - 340 °C
Mold temperature
>135 °C
Holding pressure, spec.
300 - 800 bar
Back pressure, spec.
50 - 150 bar
Injection speed
medium to high
Screw speed
8 - 15 m/min
Applications
Explore more exciting application examples that illustrate how our products can be beneficial to you in various situations and industries.
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.