Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/m²
558 Compounds found
Recommended  
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMID®

Preliminary

C28 GF 25 FRT blue (7986)

PA-Blend

AKROMID® C28 GF 25 FRT blue (7986) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 5002, Public Transportation EN 45545-2.

Modulus

11.000MPa

Strength

145MPa

Impact

60kJ/m²

AKROMID® C28 GF 25 FRT blue (7986) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 5002, Public Transportation EN 45545-2.

AKROMID®

Preliminary

B3 GF 40 1 black (8353)

PA6 GF40

AKROMID® B3 GF 40 1 black (8353) - PA 6, 40% glass fiber reinforced with excellent bonding to LSR, low emission and heat stabilised

Modulus

13.000MPa

Strength

195MPa

Impact

100kJ/m²

AKROMID® B3 GF 40 1 black (8353) - PA 6, 40% glass fiber reinforced with excellent bonding to LSR, low emission and heat stabilised

AKROMID®

C3 GF 30 1 black (4363)

PA66+PA6 GF30

AKROMID® C3 GF 30 1 black (4363) - PA6.6/6 blend, 30% glass fiber reinforced, heat stabilised, industrial engineering, automotive industry

Modulus

9.300MPa

Strength

185MPa

Impact

75kJ/m²

AKROMID® C3 GF 30 1 black (4363) - PA6.6/6 blend, 30% glass fiber reinforced, heat stabilised, industrial engineering, automotive industry

AKROMID®

B3 GF 30 S1 LA black (4446)

PA6-I GF30

AKROMID® B3 GF 30 S1 LA black (4446) - PA 6, 30% glass fiber reinforced, impact modified, laser markable, housings, covers, automotive

Modulus

8.400MPa

Strength

150MPa

Impact

110kJ/m²

AKROMID® B3 GF 30 S1 LA black (4446) - PA 6, 30% glass fiber reinforced, impact modified, laser markable, housings, covers, automotive

AKROMID®

B3 GF 30 1 EN black (5637)

PA6 GF30

AKROMID® B3 GF 30 1 EN black (5637) - 30% glass fiber reinforced PA 6, electrically neutral, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

10.300MPa

Strength

185MPa

Impact

95kJ/m²

AKROMID® B3 GF 30 1 EN black (5637) - 30% glass fiber reinforced PA 6, electrically neutral, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

T5 GF 50 black (6247)

PPA GF50

AKROMID® T5 GF 50 black (6247) - 50% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

Modulus

19.000MPa

Strength

275MPa

Impact

90kJ/m²

AKROMID® T5 GF 50 black (6247) - 50% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

PRECITE®

Preliminary

E ICF 20 black (7428)

PET CF20

PRECITE® E ICF 20 black (7428) - PET, 20% recycled carbon fibre , very high stiffness and toughness, improved surface finish, good dimensionstability, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.

Modulus

17.000MPa

Strength

180MPa

Impact

41kJ/m²

PRECITE® E ICF 20 black (7428) - PET, 20% recycled carbon fibre , very high stiffness and toughness, improved surface finish, good dimensionstability, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.

120212280

AKROLOY®

UL

PARA GF 50 HU natural (8595)PARA GF50

AKROLOY® PARA GF 50 HU natural (8595) is a 50% glass fibre reinforced polyarylamid with very high stiffness and strength, even in conditioned state owing to its lower moisture uptake. Furthermore, the material shows very good flowability and surface properties. It is perfectly suitable for parts where dimensional stabilitiy is required. Besides, it can be used as an alternative for aluminium and zinc diecast alloys. The material is listed at UL in all colors.

Features

reduced moisture
easy flow
metal substitution

Regulatory

ul

Properties

Modulus

19.000MPa

Strength

310MPa

Impact

80kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
19000 MPa
19000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
310 MPa
280 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,3 %
2,3 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
20000 MPa
20000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
445 MPa
410 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
80 kJ/m²
100 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
19 kJ/m²
18 kJ/m²

Thermal Properties

RTI electrical

UL 746B

0,8mm Wall thickness
1,6mm Wall thickness
3,2mm Wall thickness
65 °C
65 °C
65 °C

RTI impact

UL 746B

0,8mm Wall thickness
1,6mm Wall thickness
3,2mm Wall thickness
65 °C
65 °C
65 °C

RTI strength

UL 746B

0,8mm Wall thickness
1,6mm Wall thickness
3,2mm Wall thickness
65 °C
65 °C
65 °C

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
230 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
200 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
238 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
HB Class
HB Class
HB Class

HWI

UL 746A

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
4 PLC
2 PLC
2 PLC

HAI

UL 746A

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
0 PLC
0 PLC
0 PLC

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,65 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,8 %

Water absorption

ISO 62

23°C, saturated
3,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,2 %
0,2 - 0,4 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
> 600 V

Dielectric strength

IEC 60243

3 mm
31 kV/mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more