AKROMID®

Preliminary

C28 GF 25 FRT blue (7986)

PA-Blend

AKROMID® C28 GF 25 FRT blue (7986) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 5002, Public Transportation EN 45545-2.

Modulus

11.000MPa

Strength

145MPa

Impact

60kJ/m²

AKROMID® C28 GF 25 FRT blue (7986) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 5002, Public Transportation EN 45545-2.

AKROMID®

Preliminary

B3 GF 40 1 black (8353)

PA6 GF40

AKROMID® B3 GF 40 1 black (8353) - PA 6, 40% glass fiber reinforced with excellent bonding to LSR, low emission and heat stabilised

Modulus

13.000MPa

Strength

195MPa

Impact

100kJ/m²

AKROMID® B3 GF 40 1 black (8353) - PA 6, 40% glass fiber reinforced with excellent bonding to LSR, low emission and heat stabilised

AKROMID®

C3 GF 30 1 black (4363)

PA66+PA6 GF30

AKROMID® C3 GF 30 1 black (4363) - PA6.6/6 blend, 30% glass fiber reinforced, heat stabilised, industrial engineering, automotive industry

Modulus

9.300MPa

Strength

185MPa

Impact

75kJ/m²

AKROMID® C3 GF 30 1 black (4363) - PA6.6/6 blend, 30% glass fiber reinforced, heat stabilised, industrial engineering, automotive industry

AKROMID®

B3 GF 30 S1 LA black (4446)

PA6-I GF30

AKROMID® B3 GF 30 S1 LA black (4446) - PA 6, 30% glass fiber reinforced, impact modified, laser markable, housings, covers, automotive

Modulus

8.400MPa

Strength

150MPa

Impact

110kJ/m²

AKROMID® B3 GF 30 S1 LA black (4446) - PA 6, 30% glass fiber reinforced, impact modified, laser markable, housings, covers, automotive

AKROMID®

B3 GF 30 1 EN black (5637)

PA6 GF30

AKROMID® B3 GF 30 1 EN black (5637) - 30% glass fiber reinforced PA 6, electrically neutral, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

10.300MPa

Strength

185MPa

Impact

95kJ/m²

AKROMID® B3 GF 30 1 EN black (5637) - 30% glass fiber reinforced PA 6, electrically neutral, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

T5 GF 50 black (6247)

PPA GF50

AKROMID® T5 GF 50 black (6247) - 50% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

Modulus

19.000MPa

Strength

275MPa

Impact

90kJ/m²

AKROMID® T5 GF 50 black (6247) - 50% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

PRECITE®

Preliminary

E ICF 20 black (7428)

PET CF20

PRECITE® E ICF 20 black (7428) - PET, 20% recycled carbon fibre , very high stiffness and toughness, improved surface finish, good dimensionstability, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.

Modulus

17.000MPa

Strength

180MPa

Impact

41kJ/m²

PRECITE® E ICF 20 black (7428) - PET, 20% recycled carbon fibre , very high stiffness and toughness, improved surface finish, good dimensionstability, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.

120212280

AKROMID®

UL

B3 1 black (6528)PA6

AKROMID® B3 1 black (6528) is an unreinforced, heat stabilised polyamide 6

Features

heat stabilised 130

Regulatory

ul

Properties

Modulus

3.600MPa

Strength

85MPa

Impact

180kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
3600 MPa
1200 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
85 MPa
45 MPa

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
20 %
> 50 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
3100 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
120 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
no break
no break
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
5 kJ/m²
16 kJ/m²
2 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
60 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
180 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
100 - 140 °C
90 - 120 °C

Flammability

Burning rate

UL 94

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
HB Class
HB Class
V-2 Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
750 °C

GWIT

IEC 60695-2-13

1,6 mm Wall thickness
675 °C

HWI

UL 746A

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
4 PLC
3 PLC
3 PLC

HAI

UL 746A

UL
0,8 mm Wall thickness
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
1 PLC
1 PLC
0 PLC

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,13 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,6 - 3,4 %

Molding shrinkage

ISO 294-4

flow
transverse
1,0 - 1,2 %
1,1 - 1,3 %

Electrical Properties

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
1012 Ω
1010 Ω

Comparative tracking index

IEC 60112

UL
Test liquid A
600 V

Comparative tracking index

ASTM D3638

UL
0 PLC

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more