AKROMID®

Preliminary

A3 GF 30 6 ECO black (8160)

PA6.6 GF30

AKROMID® A3 GF 30 6 ECO black (8160) - PA 6.6, 30% glass fiber, recycling, high stiffness and strength, laser-markable, automotive, mechanical engineering.

Modulus

9.000MPa

Strength

150MPa

Impact

50kJ/m²

AKROMID® A3 GF 30 6 ECO black (8160) - PA 6.6, 30% glass fiber, recycling, high stiffness and strength, laser-markable, automotive, mechanical engineering.

PRECITE®

Preliminary

P3 8 natural (7517)

PBT

PRECITE® P3 8 natural (7517) - PBT, unreinforced, food contact, medium viscosity, good dimensional stability, FDA, EU10/2011, cosmetic, E&E, appliances industries.

Modulus

2.400MPa

Strength

55MPa

Impact

180kJ/m²

PRECITE® P3 8 natural (7517) - PBT, unreinforced, food contact, medium viscosity, good dimensional stability, FDA, EU10/2011, cosmetic, E&E, appliances industries.

PRECITE®

Preliminary

P3 8 black (8191)

PBT

PRECITE® P3 8 black (8191)- PBT, unreinforced, food contact, medium viscosity, good dimensional stability, FDA, EU10/2011, cosmetic, E&E, appliances industries.

Modulus

2.550MPa

Strength

60MPa

Impact

90kJ/m²

PRECITE® P3 8 black (8191)- PBT, unreinforced, food contact, medium viscosity, good dimensional stability, FDA, EU10/2011, cosmetic, E&E, appliances industries.

AKROMID®

B3 GF 30 S1 LA black (4446)

PA6-I GF30

AKROMID® B3 GF 30 S1 LA black (4446) - PA 6, 30% glass fiber reinforced, impact modified, laser markable, housings, covers, automotive

Modulus

8.400MPa

Strength

150MPa

Impact

110kJ/m²

AKROMID® B3 GF 30 S1 LA black (4446) - PA 6, 30% glass fiber reinforced, impact modified, laser markable, housings, covers, automotive

AKROMID®

B28 GF 15 2 black (7060)

PA6 GF15

AKROMID® B28 GF 15 2 black (7060) - 15% glass fibre reinforced, heat- and UV-stabilised, easy flowing polyamide 6, average stiffness and strength, passes ISO 4892-2 with 1200h exposure time.

Modulus

6.100MPa

Strength

108MPa

Impact

32kJ/m²

AKROMID® B28 GF 15 2 black (7060) - 15% glass fibre reinforced, heat- and UV-stabilised, easy flowing polyamide 6, average stiffness and strength, passes ISO 4892-2 with 1200h exposure time.

AKROMID®

B3 GF 25 FR natural (7647)

PA6 GF25 FR(40)

AKROMID® B3 GF 25 FR natural (7647) is a 25% glass fibre reinforced, halogene free flame retardant polyamide 6 with flammability acc UL 94 V0.

Modulus

9.500MPa

Strength

128MPa

Impact

73kJ/m²

AKROMID® B3 GF 25 FR natural (7647) is a 25% glass fibre reinforced, halogene free flame retardant polyamide 6 with flammability acc UL 94 V0.

PRECITE®

V GF 30 2 black (7724)

PBT+ASA GF30

PRECITE® V GF 30 2 black (7724) - PBT/ASA blend, low warpage, good surface, lower density.

Modulus

9.500MPa

Strength

130MPa

Impact

60kJ/m²

PRECITE® V GF 30 2 black (7724) - PBT/ASA blend, low warpage, good surface, lower density.

120212280

AKROLOY®

PA ICF 30 black (5269)PA66+PA6I/6T CF30

AKROLOY® PA ICF 30 black (5269) is a 30% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.

Features

low warpage
reduced moisture

Properties

Modulus

25.000MPa

Strength

220MPa

Impact

50kJ/m²

Sustainability

Recycled content

30 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
25000 MPa
23000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
220 MPa
200 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
1,5 %
1,6 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
21000 MPa
21000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
320 MPa
300 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
2 %
2 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
50 kJ/m²
50 kJ/m²
40 kJ/m²
40 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
7 kJ/m²
7 kJ/m²
6 kJ/m²
6 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
230 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
255 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,29 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,6 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,3 - 0,5 %

Electrical Properties

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
104 Ω
104 Ω

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more