PRECITE®

Preliminary

E GF 20 black (7360)

PET GF 20

PRECITE® E GF 20 black (7360) - PET, 20 % glass fibre, good stiffness, good toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

7.800MPa

Strength

NA

Impact

35kJ/m²

PRECITE® E GF 20 black (7360) - PET, 20 % glass fibre, good stiffness, good toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

PRECITE®

Preliminary

P3 GF 40 black (7591)

PBT GF 40

PRECITE® P3 GF 40 black (7591) is a 40% glass fibre reinforced, medium viscous polybutylene terephthalate (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.

Modulus

13.000MPa

Strength

165MPa

Impact

70kJ/m²

PRECITE® P3 GF 40 black (7591) is a 40% glass fibre reinforced, medium viscous polybutylene terephthalate (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.

PRECITE®

Preliminary

E GF 30 LA black (7825)

PET GF 30

PRECITE® E GF 30 LA black (7825) ) - PET, 30% glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, laser markable, metal replacement, automotive, E&E, household.

Modulus

10.500MPa

Strength

155MPa

Impact

45kJ/m²

PRECITE® E GF 30 LA black (7825) ) - PET, 30% glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, laser markable, metal replacement, automotive, E&E, household.

AKROMID®

UL
Preliminary

A3 GF 30 HU black (7631)

PA66 GF30

AKROMID® A3 GF 30 HU black (7631) is a 30% glass fibre reinforced, electrical neutral heat stabilised polyamide 6.6 with high stiffness and strength, listet at UL in all colors.

Modulus

10.000MPa

Strength

200MPa

Impact

75kJ/m²

AKROMID® A3 GF 30 HU black (7631) is a 30% glass fibre reinforced, electrical neutral heat stabilised polyamide 6.6 with high stiffness and strength, listet at UL in all colors.

AKROMID®

C28 GF 25 FRT grey (7560)

PA-Blend

AKROMID® C28 GF 25 FRT grey (7560) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 000 35 00,Public Transportation EN 45545-2.

Modulus

11.000MPa

Strength

135MPa

Impact

60kJ/m²

AKROMID® C28 GF 25 FRT grey (7560) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 000 35 00,Public Transportation EN 45545-2.

AKROMID®

A3 GF 50 1 grey (8192)

PA66 GF50

AKROMID® A3 GF 50 grey (8192) - 50% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

17.000MPa

Strength

260MPa

Impact

90kJ/m²

AKROMID® A3 GF 50 grey (8192) - 50% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROLOY®

PA GF 40 black (6416)

PA66+PA6I/6T GF40

AKROLOY® PA GF 40 black (6416) is a 40% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

Modulus

13.000MPa

Strength

235MPa

Impact

95kJ/m²

AKROLOY® PA GF 40 black (6416) is a 40% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

120212280

AKROMID®

B3 GF 30 S1 LA black (4446)PA6-I GF30

AKROMID® B3 GF 30 S1 LA black (4446) is a 30% glass fiber reinforced, impact modified Polyamide 6. It is characterised by a medium impact strength as well as a high stiffness and strength. Furthermore, the material impresses with its laser markability and is perfectly suitable for housings and covers in the automotive industry.

Features

impact modified
laser markable

Properties

Modulus

8.400MPa

Strength

150MPa

Impact

110kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
8400 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
150 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
8000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
250 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
4,8 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
30°C | d.a.m.
-
110 kJ/m²
110 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
30°C | d.a.m.
-
25 kJ/m²
15 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
205 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
145 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
222 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,33 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,3 - 1,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.