AKROMID®

Preliminary

T5 GF 35 6 natural (8005)

PPA GF35

AKROMID® T5 GF 35 6 natural (8005) is a 35% glass fibre reinforced, inorganic high temperature stabilised polyphthalamide with high rigidity and strength, as well as high temperature and chemical resistance

Modulus

12.500MPa

Strength

230MPa

Impact

70kJ/m²

AKROMID® T5 GF 35 6 natural (8005) is a 35% glass fibre reinforced, inorganic high temperature stabilised polyphthalamide with high rigidity and strength, as well as high temperature and chemical resistance

AKROMID®

Preliminary

A3 GF 30 6 ECO black (8160)

PA6.6 GF30

AKROMID® A3 GF 30 6 ECO black (8160) - PA 6.6, 30% glass fiber, recycling, high stiffness and strength, laser-markable, automotive, mechanical engineering.

Modulus

9.000MPa

Strength

150MPa

Impact

50kJ/m²

AKROMID® A3 GF 30 6 ECO black (8160) - PA 6.6, 30% glass fiber, recycling, high stiffness and strength, laser-markable, automotive, mechanical engineering.

AKROMID®

B3 ICF 15 black (5026)

PA6 CF15

AKROMID® B3 ICF 15 black (5026) is a 15% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties.

Modulus

11.000MPa

Strength

140MPa

Impact

55kJ/m²

AKROMID® B3 ICF 15 black (5026) is a 15% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties.

AKROMID®

A3 GF 50 1 grey (8192)

PA66 GF50

AKROMID® A3 GF 50 grey (8192) - 50% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

17.000MPa

Strength

260MPa

Impact

90kJ/m²

AKROMID® A3 GF 50 grey (8192) - 50% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

PRECITE®

Preliminary

E GF 45 ECO black (8284)

PET GF45

PRECITE® E GF 45 ECO black (8284) - PET, 45% glass fiber, very high stiffness, high toughness, good dimensional stability, good chemical resistance, automotive, E&E, industrial, household, sport & leisure.

Modulus

16.100MPa

Strength

200MPa

Impact

65kJ/m²

PRECITE® E GF 45 ECO black (8284) - PET, 45% glass fiber, very high stiffness, high toughness, good dimensional stability, good chemical resistance, automotive, E&E, industrial, household, sport & leisure.

AKROMID®

B3 GF 60 4 RM-M natural (4645)

PA6 + X GF60

AKROMID® B3 GF 60 4 RM-M natural (4645) is a 60% glass fiber reinforced, hydrolysis- and chemical stabilised polyamide 6 with low humidity absorption, very good surface finish and light inherent color.

Modulus

21.500MPa

Strength

235MPa

Impact

65kJ/m²

AKROMID® B3 GF 60 4 RM-M natural (4645) is a 60% glass fiber reinforced, hydrolysis- and chemical stabilised polyamide 6 with low humidity absorption, very good surface finish and light inherent color.

AKROMID®

B3 GF 15 1 L black (4670)

PA6+PP GF15

AKROMID® B3 GF 15 1 L black (4670) - PA6/PP-Blend 15% glass fibre reinforced, lower density, cost reduced, calcium chloride

Modulus

5.200MPa

Strength

105MPa

Impact

60kJ/m²

AKROMID® B3 GF 15 1 L black (4670) - PA6/PP-Blend 15% glass fibre reinforced, lower density, cost reduced, calcium chloride

120212280

AKROMID®

B3 GF 20 black (2491)PA6 GF20

AKROMID® B3 GF 20 black (2491) is a 20% glass fibre reinforced polyamide 6 with medium stiffness and strength

Properties

Modulus

6.800MPa

Strength

150MPa

Impact

73kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
6800 MPa
4200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
150 MPa
85 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,5 %
7,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
6100 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
230 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
73 kJ/m²
88 kJ/m²
65 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
9 kJ/m²
14 kJ/m²
8 kJ/m²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.
200 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
210 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
160 - 175 °C
130 - 150 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
650 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,27 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,4 - 2,7 %

Water absorption

ISO 62

23°C, saturated
7,4 - 7,7 %

Molding shrinkage

ISO 294-4

flow
transverse
0,2 %
0,8 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
conditioned
1013 Ω x cm
1010 Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
1012 Ω
1010 Ω

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.