AKROMIDĀ®

Preliminary

C28 GF 25 FRT blue (7986)

PA-Blend

AKROMIDĀ® C28 GF 25 FRT blue (7986) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 5002, Public Transportation EN 45545-2.

Modulus

11.000MPa

Strength

145MPa

Impact

60kJ/mĀ²

AKROMIDĀ® C28 GF 25 FRT blue (7986) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 5002, Public Transportation EN 45545-2.

AKROMIDĀ®

Preliminary

B3 GF 40 1 black (8353)

PA6 GF40

AKROMIDĀ® B3 GF 40 1 black (8353) - PA 6, 40% glass fiber reinforced with excellent bonding to LSR, low emission and heat stabilised

Modulus

13.000MPa

Strength

195MPa

Impact

100kJ/mĀ²

AKROMIDĀ® B3 GF 40 1 black (8353) - PA 6, 40% glass fiber reinforced with excellent bonding to LSR, low emission and heat stabilised

AKROMIDĀ®

C3 GF 30 1 black (4363)

PA66+PA6 GF30

AKROMIDĀ® C3 GF 30 1 black (4363) - PA6.6/6 blend, 30% glass fiber reinforced, heat stabilised, industrial engineering, automotive industry

Modulus

9.300MPa

Strength

185MPa

Impact

75kJ/mĀ²

AKROMIDĀ® C3 GF 30 1 black (4363) - PA6.6/6 blend, 30% glass fiber reinforced, heat stabilised, industrial engineering, automotive industry

AKROMIDĀ®

B3 GF 30 S1 LA black (4446)

PA6-I GF30

AKROMIDĀ® B3 GF 30 S1 LA black (4446) - PA 6, 30% glass fiber reinforced, impact modified, laser markable, housings, covers, automotive

Modulus

8.400MPa

Strength

150MPa

Impact

110kJ/mĀ²

AKROMIDĀ® B3 GF 30 S1 LA black (4446) - PA 6, 30% glass fiber reinforced, impact modified, laser markable, housings, covers, automotive

AKROMIDĀ®

B3 GF 30 1 EN black (5637)

PA6 GF30

AKROMIDĀ® B3 GF 30 1 EN black (5637) - 30% glass fiber reinforced PA 6, electrically neutral, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

10.300MPa

Strength

185MPa

Impact

95kJ/mĀ²

AKROMIDĀ® B3 GF 30 1 EN black (5637) - 30% glass fiber reinforced PA 6, electrically neutral, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMIDĀ®

T5 GF 50 black (6247)

PPA GF50

AKROMIDĀ® T5 GF 50 black (6247) - 50% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

Modulus

19.000MPa

Strength

275MPa

Impact

90kJ/mĀ²

AKROMIDĀ® T5 GF 50 black (6247) - 50% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

PRECITEĀ®

Preliminary

E ICF 20 black (7428)

PET CF20

PRECITEĀ® E ICF 20 black (7428) - PET, 20% recycled carbon fibre , very high stiffness and toughness, improved surface finish, good dimensionstability, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.

Modulus

17.000MPa

Strength

180MPa

Impact

41kJ/mĀ²

PRECITEĀ® E ICF 20 black (7428) - PET, 20% recycled carbon fibre , very high stiffness and toughness, improved surface finish, good dimensionstability, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.

120212280

AKROMIDĀ®

B3 GFM 15/25 black (1312)PA6 (GF15+MD25)

AKROMIDĀ® B3 GFM 15/25 black (1312) is a 15% glass fibre reinforced, 25% mineral filled polyamide 6 with good surface and dimensional stability

Features

surface modified
low warpage

Properties

Modulus

8.000MPa

Strength

120MPa

Impact

50kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
8000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
120 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
3 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
7000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
190 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
50 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
4 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
190 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
216 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
222 Ā°C

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
160 - 175 Ā°C
130 - 150 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,45 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,8 %

Water absorption

ISO 62

23Ā°C, saturated
6,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 %
0,9 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
1012 ā„¦ x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1015 ā„¦

Comparative tracking index

IEC 60112

Test liquid A
400 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more