PA6 – Polyamide 6 PA6 GF10 + GB20
AKROMID® B28 GM 10/20 1 LA black (4790)AKROMID® B28 GM 10/20 1 LA black (4790) is a 10% glass fiber and 20% glass beads reinforced easy flowing PA 6. It is characterised by a medium stiffness and strength.
The material impresses with its laser markability along with very good surface properties and is therefore perfectly suitable for housings and covers in the automotive industry with high demands on the surface.
Properties
Tensile Modulus Tensile Strength Impact StrengthFeatures
-
Mechanical Properties
Tensile modulus (1 mm/min | ISO 527-2) d.a.m. 5700 MPa conditioned 3000 MPa
Stress at break (5 mm/min | ISO 527-2) d.a.m. 110 MPa conditioned 60 MPa
Strain at break (5 mm/min | ISO 527-2) d.a.m. 2,6 % conditioned 10 %
Flexural modulus (2 mm/min | ISO 178) d.a.m. 5000 MPa
Flexural strength (2 mm/min | ISO 178) d.a.m. 170 MPa
Charpy impact strength (23°C | ISO 179-1/1eU) d.a.m. 30 kJ/m² conditioned 80 kJ/m²
Charpy impact strength (-30°C | ISO 179-1/1eU) d.a.m. 30 kJ/m²
Charpy notched impact strength (23°C | ISO 179-1/1eA) d.a.m. 4 kJ/m² conditioned 7 kJ/m²
Charpy notched impact strength (-30°C | ISO 179-1/1eA) d.a.m. 4 kJ/m²
-
Thermal Properties
Temperature of deflection under load HDT/A (1,8 MPa | ISO 75) 200 °C
Melting temperature (DSC, 10K/min | DIN EN ISO 11357-3) 222 °C
Coefficent of linear thermal expansion, parallel (23°C bis 80°C | ISO 11359-1/2) 0,34 1,0E-4/K
Coefficent of linear thermal expansion, transverse (23°C bis 80°C | ISO 11359-1/2) 1,02 1,0E-4/K
-
Flammability
Burning rate (UL 94) 1,6mm Wall thickness HB Class
GWFI (IEC 60695-2-12) 1,6mm Wall thickness 650 °C
Burning rate (<100 mm/min) (> 1 mm Thickness | FMVSS 302) +
-
General properties
Density (23°C | ISO 1183) 1,35 g/cm³
Humidity absorption (70°C, 62% r.H. | ISO 1110) 2,2 %
Molding shrinkage (flow | ISO 294-4) 0,3-0,5 %
Molding shrinkage (transverse | ISO 294-4) 0,6-0,8 %
-
Electrical Properties
Surface resistivity (DIN EN 62631-3-2) d.a.m. 1,0E+5 Ω
-
Sustainability
Recycled content (at least) 20 %
Processing information
The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.
Drying time | 0 - 4 h | |
Drying temperature (τ ≤ -30°C) | 80°C | |
Processing moisture | 0,02 - 0,1% | |
Feed section | 60 - 80°C | |
Temperature zone 1 - Zone 4 | 240 - 290°C | |
Nozzle temperature | 260 - 300°C | |
Melt temperature | 270 - 290°C | |
Mold temperature | 80 - 100°C | |
Holding pressure, spec. | 300 - 800 bar | |
Back pressure, spec. | 50 - 150 bar | |
Injection speed | medium to high | |
Screw speed | 8 - 15 m/min | |
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.