PA6 – Polyamide 6 PA6 GF30
AKROMID® B3 GF 30 1 GIT black (4598)
AKROMID® B3 GF 30 1 GIT black (4598) is a 30% glass fibre reinforced, heat stabilised polyamide 6 with high stiffness and strength for gas injection technology.
Engineering parts, which are produced by gas injection technology. Furthermore B3 GF 30 1 GIT black (4598) can be used for standard injection moulding for demanding surface quality.
The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.
|Drying time||0 - 4 h|
|Drying temperature (τ ≤ -30°C)||80°C|
|Processing moisture||0,02 - 0,1%|
|Feed section||60 - 80°C|
|Temperature zone 1 - Zone 4||240 - 290°C|
|Nozzle temperature||260 - 300°C|
|Melting temperature||270 - 290°C|
|Mold temperature||80 - 100°C|
|Holding pressure, spec.||300 - 800 bar|
|Back pressure, spec.||50 - 150 bar|
|Injection speed||medium to high|
|Screw speed||8 - 15 m/min|
- Mechanical Properties
Tensile modulus (1 mm/min | ISO 527-2) d.a.m. 9500 MPa conditioned 6000 MPa Stress at break (5 mm/min | ISO 527-2) d.a.m. 175 MPa conditioned 110 MPa Strain at break (5 mm/min | ISO 527-2) d.a.m. 3,0 % conditioned 5,5 %
- Thermal Properties
Temperature of deflection under load HDT/A (1,8 MPa | ISO 75) 210 °C Temperature of deflection under load HDT/B (0,45 MPa | ISO 75) 220 °C Melting temperature (DSC, 10K/min | DIN EN 11357-1) 220 °C
Burning rate (UL 94) 0,8mm Wall thickness HB Class Burning rate (<100 mm/min) (> 1 mm Thickness | FMVSS 302) +
- General properties
Density (23°C | ISO 1183) 1,36 g/cm³ Humidity absorption (70°C, 62% r.F. | ISO 1110) 2,1 % Molding shrinkage (flow | ISO 294-4) 0,1 - 0,3 % Molding shrinkage (transverse | ISO 294-4) 0,5 - 0,7 %
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.