T9 GFM 40/15 black (8209)PPA GF40 + M15

AKROMID® T9 GFM 40/15 black (8209) is a 40% glass fibre reinforced, 15% mineral filled, polyphthalamide with very good surface and low warpage, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.

Features

low warpage
reduced moisture

Properties

Modulus

16.000MPa

Strength

170MPa

Impact

40kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
16000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
170 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
1,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
40 kJ/m²

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
300 °C

Flammability

Flammability

UL 94

1,6 mm Wall thickness
HB Class

General Properties

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,4 - 0,6 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.