AKROMID®

Internal

T5 GF 50 8 natural (6464)PPA GF50

AKROMID® T5 GF 50 8 natural (6464) is a 50% glass fibre reinforced polyphthalamide with good chemical resistance. This aromatic PPA keeps mechanical performance even at elevated temperatures as well as moisture pic-up. The material fulfills the requirements according to NSF 61. This material corresponds to the European food guideline EU 10/2011 and to the American FDA 21 CFR and is suitable for parts of kitchen and household appliances.

Regulatory

eu102011fdansf-coldnsf-hot

Properties

Modulus

18.000MPa

Strength

300MPa

Impact

105kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
18000 MPa
18000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
300 MPa
300 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,5 %
2,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
18500 MPa
18500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
410 MPa
350 MPa

Standard bending strength RP 3,5

ISO 178

2mm/min | d.a.m.
2,5 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
105 kJ/m²
105 kJ/m²
75 kJ/m²
75 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
13 kJ/m²
13 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
280 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
325 °C

Flammability

Flammability

UL 94

1,6 mm Wall thickness
HB Class

General Properties

Density

ISO 1183

23°C
1,65 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,8 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,4 - 0,6 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.