AKROMID®

Preliminary

NEXT G3 GF 30 1 black (8468)PA6.9 GF30

The partly bio-based AKROMID® NEXT G3 GF 30 1 black (8468) has an increased chemical resistance and a lower moisture absorption compared to the classic PA 6 and PA 6.6. This heat stabilised and 30% glass fibre reinforced PA 6.9 is suitable for components with high demands on strength and stiffness.

Features

Bio-based
heat stabilised 130
electrically neutral
reduced moisture

Properties

Modulus

8.600MPa

Strength

160MPa

Impact

80kJ/m²

Sustainability


Biobased carbon content

55 %

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
8600 MPa
6300 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
160 MPa
120 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,8 %
5,3 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
8300 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
250 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
4,8 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
80 kJ/m²
80 kJ/m²
70 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
13 kJ/m²
14 kJ/m²
11 kJ/m²

Thermal Properties


Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
195 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
219 °C

General properties


Density

ISO 1183

23°C
1,31 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,1 - 1,3 %

Water absorption

ISO 62

23°C, saturated
3,0 - 3,4 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,7 - 0,9 %

Rheological Properties


Flowability

AKRO

2 mm Thickness
420 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.