AKROMID®

UL

C3 1 FR black (5266)PA66 + PA 6 FR (30)

AKROMID® C3 1 FR black (5266) is a unreinforced, flame retardant and heat stabilised PA6/6.6 blend. Listed to UL 94 in all-colours, the material is based on a flame retardant system that is free of red phosphorus and halogens. Due to its good flowability, an improved surface quality is achieved and it is quite suitable for film hinges. This grade meets the requirements for public transportation (EN 45545-2 and ISO 4589-2) and is also suitable for applications in the automotive and E&E markets.

Features

heat stabilised 130
flame retardant
surface modified
easy flow
E&E
public transportation

Regulatory

ul

Properties

Modulus

3.400MPa

Strength

75MPa

Impact

100kJ/m²

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
3400 MPa
1300 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
75 MPa
40 MPa

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
> 10 %
> 50 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
> 100
no break
90

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
30°C | d.a.m.
-
4 kJ/m²
3 kJ/m²

Thermal Properties


Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
70 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
210 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
260 °C

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
126 °C
111 °C

Flammability


UL

Burning rate

UL 94

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
V-0 Class
V-0 Class
V-0 Class
V-0 Class

GWFI

IEC 60695-2-12

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
960 °C
960 °C
960 °C
960 °C

GWIT

IEC 60695-2-13

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
750 °C
750 °C
750 °C
775 °C

UL

HWI

UL 746A

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
4 PLC
4 PLC
0 PLC
0 PLC

UL

HAI

UL 746A

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
0 PLC
0 PLC
0 PLC
0 PLC

Oxygen index

ISO 4589-2

34,5 %

Protection Train

EN 45545-2

R22 HL2 R23/24/26 HL3

General properties


Density

ISO 1183

23°C
1,16 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,1 - 2,3 %

Molding shrinkage

ISO 294-4

flow
transverse
1,1 - 1,3 %
1,2 - 1,4 %

Electrical Properties


Volume resistivity IEC

DIN EN 62631-3-2

d.a.m.
1012 Ω x cm

Comparative tracking index

IEC 60112

Test liquid A
> 600 V

Dielectric strength

IEC 60243

3 mm
10 kV/mm

Inclined-Plane Tracking, IPT

ASTM D2303-13

1 kV

UL

High voltage arc tracking rate (HVTR)

UL 746A

0 PLC

High Volt, Low Current Arc Resistance

ASTM D495

5 PLC

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.