AKROMID®

Internal

B3 ICF 15 black (7402)PA6 CF15

AKROMID® B3 ICF 15 black BMW (7402) is a 15% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties. The BMW item can only be supplied with approval from BMW for specially promoted projects. Please offer our AKROMID® B3 ICF 15 black (5026) for other projects instead.

Features

heat stabilised 130

Properties

Modulus

11.000MPa

Strength

140MPa

Impact

55kJ/m²

Sustainability

Recycled content

15 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
11000 MPa
5000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
140 MPa
80 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3 %
7 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
9000 MPa
7000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
200 MPa
150 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
2,5 %
6 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
55 kJ/m²
80 kJ/m²
45 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
6 kJ/m²
10 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
200 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Thermal conductivity

DIN 52612

0,31 W/mK

Flammability

Flammability

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General Properties

Density

ISO 1183

23°C
1,19 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,7 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 %
0,7 %

Electrical Properties

Surface resistivity

IEC 62631-3-2

d.a.m.
conditioned
105 Ω
105 Ω

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.